Comparison of Microstructure, Texture, and Mechanical Properties of TZ61 and AZ61 Mg Alloys Processed by Differential Speed Rolling
In this work, the comparison of microstructure, texture, and mechanical properties of the newly developed TZ61 (Mg-6Sn-1Zn) alloy with the commercially available AZ61 (Mg-6Al-1Zn) has been presented. Both analyzed Mg alloys were processed by conventional symmetric and asymmetric rolling (i.e., Diffe...
Autores principales: | , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2022
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8837043/ https://www.ncbi.nlm.nih.gov/pubmed/35160730 http://dx.doi.org/10.3390/ma15030785 |
Sumario: | In this work, the comparison of microstructure, texture, and mechanical properties of the newly developed TZ61 (Mg-6Sn-1Zn) alloy with the commercially available AZ61 (Mg-6Al-1Zn) has been presented. Both analyzed Mg alloys were processed by conventional symmetric and asymmetric rolling (i.e., Differential Speed Rolling—DSR). The microstructure and texture were examined by EBSD and XRD, whereas the mechanical behavior was investigated by uniaxial tensile tests. DSR processing led to more effective grain refinement of both TZ61 and AZ61 sheets. However, a high fraction of Mg(2)Sn phase precipitates in the TZ61 sheets hindered grain growth what resulted in their smaller grain size as compared to AZ61 sheets. DSR processing lowered also the basal texture intensity in the TZ61 and AZ61 sheets. A unique basal poles splitting was observed for the as-rolled TZ61 alloy, while AZ61 alloy exhibited a typical single-peak basal texture. Finally, the reduced grain size and weakened basal texture by DSR processing caused increase of plasticity of the annealed TZ61 and AZ61 sheets. Nevertheless, the annealed AZ61 sheets showed higher uniform elongation and strength (as compared to TZ61 ones), which has been attributed to their significantly lower texture intensity and greater ability to strain hardening. |
---|