Study on Solidification and Stabilization of Antimony-Containing Tailings with Metallurgical Slag-Based Binders

Blast furnace slag (BFS), steel slag (SS), and flue gas desulfurized gypsum (FGDG) were used to prepare metallurgical slag-based binder (MSB), which was afterwards mixed with high-antimony-containing mine tailings to form green mining fill samples (MBTs) for Sb solidification/stabilization (S/S). Re...

Descripción completa

Detalles Bibliográficos
Autores principales: Li, Yunyun, Ni, Wen, Gao, Wei, Zhang, Siqi, Fu, Pingfeng, Li, Yue
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2022
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8911367/
https://www.ncbi.nlm.nih.gov/pubmed/35269012
http://dx.doi.org/10.3390/ma15051780
Descripción
Sumario:Blast furnace slag (BFS), steel slag (SS), and flue gas desulfurized gypsum (FGDG) were used to prepare metallurgical slag-based binder (MSB), which was afterwards mixed with high-antimony-containing mine tailings to form green mining fill samples (MBTs) for Sb solidification/stabilization (S/S). Results showed that all MBT samples met the requirement for mining backfills. In particular, the unconfined compressive strength of MBTs increased with the curing time, exceeding that of ordinary Portland cement (OPC). Moreover, MBTs exhibited the better antimony solidifying properties, and their immobilization efficiency could reach 99%, as compared to that of OPC. KSb(OH)(6) was used to prepare pure MSB paste for solidifying mechanism analysis. Characteristics of metallurgical slag-based binder (MSB) solidified/stabilized antimony (Sb) were investigated via X-ray diffraction (XRD), field emission scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), Fourier transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS). According to the results, the main hydration products of MSB were C-S-H gel and ettringite. Among them, C-S-H gel had an obvious adsorption and physical sealing effect on Sb, and the incorporation of Sb would reduce the degree of C-S-H gel polymerization. Besides, ettringite was found to exert little impact on the solidification and stabilization of Sb. However, due to the complex composition of MSB, it was hard to conclude whether Sb entered the ettringite lattice.