Flexural Strength of CAD/CAM Denture Base Materials: Systematic Review and Meta-analysis of In-vitro Studies

INTRODUCTION: Digital complete dentures fabrication techniques are expanding. This study aimed to review flexural strength (FS) of milled and 3D-printed denture base materials to answer the study question: is FS of computer-aided designing/computer-aided manufacturing (CAD/CAM) denture base comparab...

Descripción completa

Detalles Bibliográficos
Autores principales: Abualsaud, Reem, Gad, Mohammed M.
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Wolters Kluwer - Medknow 2022
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9022382/
https://www.ncbi.nlm.nih.gov/pubmed/35462750
http://dx.doi.org/10.4103/jispcd.JISPCD_310_21
Descripción
Sumario:INTRODUCTION: Digital complete dentures fabrication techniques are expanding. This study aimed to review flexural strength (FS) of milled and 3D-printed denture base materials to answer the study question: is FS of computer-aided designing/computer-aided manufacturing (CAD/CAM) denture base comparable to conventional heat-polymerized materials? MATERIALS AND METHODS: Search was done within different databases for articles published between January 2010 and June 2021 using specific keywords. Articles of in-vitro studies in English language with methods following International Standards Organization standardization/ADA specifications for flexural testing of conventional and CAD/CAM (milled or printed) polymethyl methacrylate (PMMA) materials were included. RESULTS: Out of the 61 studies, 9 were processed for data extraction and only 7 underwent meta-analysis. Two, six, and one study showed high, moderate, and low risk of bias, respectively. Random-effects model was used for analysis and resulted in the average FS of 120.61 MPa [95% confidence interval (CI): 109.81−131.41] and 92.16 MPa (CI: 75.12−109.19) for CAD/CAM milled and heat-polymerized PMMA, respectively. CONCLUSION: Subtractive CAD/CAM technique of denture fabrication showed satisfactory FS values, whereas additive CAD/CAM method was comparable to conventional heat-polymerized technique with lower value, requiring further investigations and improvement. The clinical use of milled denture bases is an acceptable substitution to heat-polymerized PMMA, making the denture fabrication an easier and faster process.