Crack Initiation Mechanism and Life Prediction of Ti60 Titanium Alloy Considering Stress Ratios Effect in Very High Cycle Fatigue Regime

Ultrasonic fatigue tests were performed on Ti60 titanium alloy up to a very high cycle fatigue (VHCF) regime at various stress ratios to investigate the characteristics. The S-N curves showed continuous declining trends with fatigue limits of 400, 144 and 130 MPa at 10(9) cycles corresponding to str...

Descripción completa

Detalles Bibliográficos
Autores principales:	He, Ruixiang, Peng, Haotian, Liu, Fulin, Khan, Muhammad Kashif, Chen, Yao, He, Chao, Wang, Chong, Wang, Qingyuan, Liu, Yongjie
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2022
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9027182/ https://www.ncbi.nlm.nih.gov/pubmed/35454493 http://dx.doi.org/10.3390/ma15082800

Ejemplares similares

Influence of Welded Pores on Very Long-Life Fatigue Failure of the Electron Beam Welding Joint of TC17 Titanium Alloy
por: Liu, Fulin, et al.
Publicado: (2019)

Bending Fatigue Behavior of 316L Stainless Steel up to Very High Cycle Fatigue Regime
por: Hu, Yongtao, et al.
Publicado: (2020)

Internal crack characteristics in very-high-cycle fatigue of a gradient structured titanium alloy
por: Pan, Xiangnan, et al.
Publicado: (2020)

A Novel Ultrasonic Fatigue Test and Application in Bending Fatigue of TC4 Titanium Alloy
por: Tang, Sen, et al.
Publicado: (2022)

Stress Ratio and Notch Effects on the Very High Cycle Fatigue Properties of a Near-Alpha Titanium Alloy
por: Yang, Kun, et al.
Publicado: (2018)

Characterization on Crack Initiation and Early Propagation Region of Nickel-Based Alloys in Very High Cycle Fatigue
por: Chen, Zelin, et al.
Publicado: (2022)

Experimental Research on Fatigue Crack Growth Behavior of Diffusion-Bonded Titanium Alloy Laminates with Preset Unbonded Areas
por: Liu, Yang, et al.
Publicado: (2022)

Effects of Loading Frequency and Specimen Geometry on High Cycle and Very High Cycle Fatigue Life of a High Strength Titanium Alloy
por: Li, Yanqing, et al.
Publicado: (2018)

Effect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy
por: Nie, Baohua, et al.
Publicado: (2017)

Mechanism of Fatigue Crack Growth in Biomedical Alloy Ti-27Nb
por: Amjad, Muhammad, et al.
Publicado: (2020)

Fatigue Crack Initiation Change of Cast AZ91 Magnesium Alloy from Low to Very High Cycle Fatigue Region
por: Fintová, Stanislava, et al.
Publicado: (2021)

Investigation on the Fatigue Crack Propagation of Medium-Entropy Alloys with Heterogeneous Microstructures
por: Liu, Yang, et al.
Publicado: (2022)

The Influence of Porosity on Fatigue Crack Initiation in Additively Manufactured Titanium Components
por: Tammas-Williams, S., et al.
Publicado: (2017)

An Artificial Neural Network-Based Algorithm for Evaluation of Fatigue Crack Propagation Considering Nonlinear Damage Accumulation
por: Zhang, Wei, et al.
Publicado: (2016)

Influence of Pre-Stress Magnitude on Fatigue Crack Growth Behavior of Al-Alloy
por: Zhang, Chunguo, et al.
Publicado: (2018)

Study on the Cutting Performance of Micro Textured Tools on Cutting Ti-6Al-4V Titanium Alloy
por: Zheng, Kairui, et al.
Publicado: (2020)

An Approach for Predicting the Low-Cycle-Fatigue Crack Initiation Life of Ultrafine-Grained Aluminum Alloy Considering Inhomogeneous Deformation and Microscale Multiaxial Strain
por: Sun, Teng, et al.
Publicado: (2022)

Fatigue-Induced HCP-to-FCC Phase Transformation Resulting in Two FCC-Zr Variants in Pure Zirconium
por: Jiang, Qing, et al.
Publicado: (2023)

The Effect of Stress Ratios on the Very High Cycle Fatigue Behavior of 9%Cr Turbine Steel at 630 °C
por: Wang, Quanyi, et al.
Publicado: (2020)

Characterization of internal fatigue cracks in aluminum alloys by simulation of phase contrast tomography
por: Xiao, Ce, et al.
Publicado: (2022)

Prediction of Fatigue Crack Initiation of 7075 Aluminum Alloy by Crystal Plasticity Simulation
por: Shiraiwa, Takayuki, et al.
Publicado: (2023)

High temperature rise dominated cracking mechanisms in ultra-ductile and tough titanium alloy
por: Choisez, L., et al.
Publicado: (2020)

Fatigue of Beta Processed and Beta Heat-treated Titanium Alloys
por: Wanhill, Russell, et al.
Publicado: (2012)

Hydrogen-enabled microstructure and fatigue strength engineering of titanium alloys
por: Paramore, James D., et al.
Publicado: (2017)

The influence of alloying on slip intermittency and the implications for dwell fatigue in titanium
por: Worsnop, Felicity F., et al.
Publicado: (2022)

Hierarchical Dynamic Bayesian Network-Based Fatigue Crack Propagation Modeling Considering Initial Defects
por: Xu, Yang, et al.
Publicado: (2022)

Fatigue Crack Growth Rate Description of RF-Plasma-Sprayed Refractory Metals and Alloys
por: Kovarik, Ondrej, et al.
Publicado: (2023)

Cyclic Deformation and Correspondent Crack Initiation at Low-Stress Amplitudes in Mg–Gd–Y–Zr Alloy
por: He, Chao, et al.
Publicado: (2018)

Predicting dwell fatigue life in titanium alloys using modelling and experiment
por: Xu, Yilun, et al.
Publicado: (2020)

Recovery Behavior of the Macro-Cracks in Elevated Temperature-Damaged Concrete after Post-Fire Curing
por: Li, Lang, et al.
Publicado: (2022)

Low-Cycle Fatigue Crack Initiation Simulation and Life Prediction of Powder Superalloy Considering Inclusion-Matrix Interface Debonding
por: Zhang, Shuming, et al.
Publicado: (2021)

Fretting Fatigue with Cylindrical-On-Flat Contact: Crack Nucleation, Crack Path and Fatigue Life
por: Noraphaiphipaksa, Nitikorn, et al.
Publicado: (2017)

Combustion Behavior and Mechanism of Ti14 Titanium Alloy
por: Shao, Lei, et al.
Publicado: (2020)

Author Correction: Characterization of internal fatigue cracks in aluminum alloys by simulation of phase contrast tomography
por: Xiao, Ce, et al.
Publicado: (2023)

Simulation of Intergranular Ductile Cracking in β Titanium Alloys Based on a Micro-Mechanical Damage Model
por: Li, Huan, et al.
Publicado: (2017)

Effect of Oxygen Variation on High Cycle Fatigue Behavior of Ti-6Al-4V Titanium Alloy
por: Tang, Luyao, et al.
Publicado: (2020)

Residual Stress of a TC17 Titanium Alloy after Belt Grinding and Its Impact on the Fatigue Life
por: He, Yi, et al.
Publicado: (2018)

Relationship between dynamic fatigue crack propagation properties and viscoelasticity of natural rubber/silicone rubber composites
por: Han, Qingyuan, et al.
Publicado: (2019)

Influence of Fine Grains on the Bending Fatigue Behavior of Two Implant Titanium Alloys
por: Cao, Xiaojian, et al.
Publicado: (2020)

Effect of Cutting Surface Integrity on Fatigue Properties of TC17 Titanium Alloy
por: Wang, Dan, et al.
Publicado: (2023)

Cannot write session to /tmp/vufind_sessions/sess_1lsqt9s5f3tvgdvahn74nknuu4