Revisiting the valence stability and preparation of perovskite structure type oxides ABO(3) with the use of Madelung electrostatic potential energy and lattice site potential

Valence stability of aliovalent ions is mostly correlated with lattice site potential in ionic crystals. Madelung electrostatic potential is obtained by adding all the lattice site potentials for all the ions present in a crystal structure. Therefore, valence stability and the stability of a crystal...

Descripción completa

Detalles Bibliográficos
Autores principales: Yoshimura, Masahiro, Sardar, Kripasindhu
Formato: Online Artículo Texto
Lenguaje:English
Publicado: The Royal Society of Chemistry 2021
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9033973/
https://www.ncbi.nlm.nih.gov/pubmed/35479376
http://dx.doi.org/10.1039/d1ra01979a
Descripción
Sumario:Valence stability of aliovalent ions is mostly correlated with lattice site potential in ionic crystals. Madelung electrostatic potential is obtained by adding all the lattice site potentials for all the ions present in a crystal structure. Therefore, valence stability and the stability of a crystal structure can be better understood with consideration of both the lattice site potential and Madelung electrostatic potential. This was first demonstrated more than four decades ago by one of the present authors. We revisit this situation by using re-calculated lattice site potential and Madelung electrostatic potential for perovskite structure type ABO(3) compounds using a new computer program VESTA. We show that the formation of a perovskite structure type compound with the general formula ABO(3) (where A and B are cations and O is an oxide ion) becomes energetically favorable when it has a higher Madelung electrostatic potential than the combined Madelung electrostatic potential of parent binary compounds AO and B(2)O(3) or BO(2). It is further shown that strong lattice site potential results in stability of high valence or high valence ions can be stabilized in a lattice site with strong lattice-site potential. It further follows that certain ions experience maximum lattice site potential at the B ion lattice site of the perovskite structure when compared to other structures such as fluorite BO(2), rutile BO(2) and corundum B(2)O(3). Therefore, (i) the stability of an ion with a high (and uncommon) valence state at the B site being higher than that at the A site, (ii) occurrence of point defects at A or O sites with weak lattice site potentials, respectively and (iii) instability of perovskite A(4+)B(2+)O(3), and A(5+)B(1+)O(3) compounds, respectively can be rationalized by lattice site potential and Madelung electrostatic potential analysis.