Enhancement of the electrochemical performance of lithium-ion batteries by SiO(2)@poly(2-acrylamido-2-methylpropanesulfonic acid) nanosphere addition into a polypropylene membrane

Employing electrostatic self-assembly and free radical polymerization, the surface of SiO(2) nanospheres was coated with poly(2-acrylamido-2-methylpropanesulfonic acid) (SiO(2)@PAMPS) bearing strong electron withdrawing sulfonic and amide groups, enhancing the dissociation ability of the lithium salt of the liquid electrolyte and absorbing anions via hydrogen bonds. After SiO(2)@PAMPS nanospheres were introduced into the polypropylene (PP) membrane (SiO(2)@PAMPS/PP), the electrolyte affinity and electrolyte uptake of the composite separators were significantly improved. The ionic conductivity of SiO(2)@PAMPS/PP-18% (where 18% represents the concentration of the solution used for coating) soaked in liquid electrolyte was even 0.728 mS cm(−1) at 30 °C, much higher than that of the pristine PP membrane. The LiFePO(4)/Li half-cell with SiO(2)@PAMPS/PP-18% had a discharge capacity of 148.10 mA h g(−1) and retained 98.67% of the original capacity even after 120 cycles at 0.5C. Even at a rate of 1.0C, the cell capacity could be maintained above 120 mA h g(−1). Therefore, a coating formula was developed that could considerably improve the cycling ability and high rate charge–discharge performance of lithium ion batteries.