Morphology of subsurface cracks in glass-ceramics induced by Vickers indentation observed by synchrotron X-ray multiscale tomography
The characterization of subsurface cracks induced by indentation is a challenge for understanding contact damage, impact, wear, erosion, and abrasion of brittle materials, because the crack pattern observable on the surface is only a part of the total crack system. Here we applied synchrotron X-ray...
Autores principales: | Okuma, Gaku, Maeda, Kei, Yoshida, Satoshi, Takeuchi, Akihisa, Wakai, Fumihiro |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Nature Publishing Group UK
2022
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9050884/ https://www.ncbi.nlm.nih.gov/pubmed/35484320 http://dx.doi.org/10.1038/s41598-022-11084-0 |
Ejemplares similares
-
Phase-Field Modeling of Fused Silica Cone-Crack Vickers Indentation
por: Tomić, Zoran, et al.
Publicado: (2022) -
3D multiscale-imaging of processing-induced defects formed during sintering of hierarchical powder packings
por: Okuma, Gaku, et al.
Publicado: (2019) -
Bone Material Properties of Human Phalanges Using Vickers Indentation
por: Yin, Bing, et al.
Publicado: (2019) -
Crack nucleation criterion and its application to impact indentation in glasses
por: Luo, Jian, et al.
Publicado: (2016) -
Vickers, a history
por: Scott, J. D. (John Dick), 1917-
Publicado: (1962)