Effect of initial support particle size of MnO(x)/TiO(2) catalysts in the selective catalytic reduction of NO with NH(3)

A series of manganese-based catalysts supported by 5–10 nm, 10–25 nm, 40 nm and 60 nm anatase TiO(2) particles was synthesized via an impregnation method to investigate the effect of the initial support particle size on the selective catalytic reduction (SCR) of NO with NH(3). All catalysts were cha...

Descripción completa

Detalles Bibliográficos
Autores principales:	Yang, Yang, Hu, Zhun, Mi, Rongli, Li, Dan, Yong, Xiang, Yang, Huie, Liu, Kunfeng
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	The Royal Society of Chemistry 2019
Materias:	Chemistry
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9060628/ https://www.ncbi.nlm.nih.gov/pubmed/35514617 http://dx.doi.org/10.1039/c8ra10077b

Ejemplares similares

Catalytic Oxidation of NO over MnO(x)–CeO(2) and MnO(x)–TiO(2) Catalysts
por: Zeng, Xiaolan, et al.
Publicado: (2016)

Reverse Micelle Strategy for the Synthesis of MnO(x)–TiO(2) Active Catalysts for NH(3)-Selective Catalytic Reduction of NO(x) at Both Low Temperature and Low Mn Content
por: Bonelli, Barbara, et al.
Publicado: (2021)

Insight into the synergism between MnO(2) and acid sites over Mn–SiO(2)@TiO(2) nano-cups for low-temperature selective catalytic reduction of NO with NH(3)
por: Zheng, Siyi, et al.
Publicado: (2018)

Modification of V(2)O(5)-WO(3)/TiO(2) Catalyst by Loading of MnO(x) for Enhanced Low-Temperature NH(3)-SCR Performance
por: Zhang, Xianlong, et al.
Publicado: (2020)

Sulfur resistance of Ce-Mn/TiO(2) catalysts for low-temperature NH(3)–SCR
por: Xu, Quan, et al.
Publicado: (2018)

Deactivation by HCl of CeO(2)–MoO(3)/TiO(2) catalyst for selective catalytic reduction of NO with NH(3)
por: Jiang, Ye, et al.
Publicado: (2018)

Effect of Calcination Temperature on the Activation Performance and Reaction Mechanism of Ce–Mn–Ru/TiO(2) Catalysts for Selective Catalytic Reduction of NO with NH(3)
por: Ren, Zhixiang, et al.
Publicado: (2020)

Low-temperature selective catalytic reduction of NO with NH(3) over an FeO(x)/β-MnO(2) composite
por: Du, Bo, et al.
Publicado: (2023)

CeO(2) Nanoparticle-Loaded MnO(2) Nanoflowers for Selective Catalytic Reduction of NO(x) with NH(3) at Low Temperatures
por: Li, Shun, et al.
Publicado: (2022)

Promotion effect of urchin-like MnO(x)@PrO(x) hollow core–shell structure catalysts for the low-temperature selective catalytic reduction of NO with NH(3)
por: Cheng, Shuyuan, et al.
Publicado: (2020)

Sulfation effect of Ce/TiO(2) catalyst for the selective catalytic reduction of NO(x) with NH(3): mechanism and kinetic studies
por: Zhang, Wenjie, et al.
Publicado: (2019)

Spatial separation of oxidation and reduction co-catalysts for efficient charge separation: Pt@TiO(2)@MnO( x ) hollow spheres for photocatalytic reactions
por: Li, Ang, et al.
Publicado: (2016)

Catalytic oxidation of NO over MnO(x)–CoO(x)/TiO(2) in the presence of a low ratio of O(3)/NO: activity and mechanism
por: Si, Meng, et al.
Publicado: (2020)

Unravelling the Catalytic Activity of MnO(2), TiO(2), and VO(2) (110) Surfaces by Oxygen Coadsorption on Sodium-Adsorbed MO(2) {M = Mn, Ti, V}
por: Maenetja, Khomotso P., et al.
Publicado: (2022)

Different morphologies on Cu–Ce/TiO(2) catalysts for the selective catalytic reduction of NO(x) with NH(3) and DRIFTS study on sol–gel nanoparticles
por: Zhuang, Ke, et al.
Publicado: (2023)

Synthesis of Both Powdered and Preformed MnO(x)–CeO(2)–Al(2)O(3) Catalysts by Self-Propagating High-Temperature Synthesis for the Selective Catalytic Reduction of NO(x) with NH(3)
por: Wang, Chao, et al.
Publicado: (2018)

Activation of Water on MnO(x)-Nanocluster-Modified Rutile (110) and Anatase (101) TiO(2) and the Role of Cation Reduction
por: Rhatigan, Stephen, et al.
Publicado: (2019)

Surface protection against corrosion of Ni turbine blades by electrophoretic deposition of MnO(2), TiO(2) and TiO(2)–C nanocoating
por: Yousif, Qahtan. A., et al.
Publicado: (2022)

Fe(2)O(3) enhanced high-temperature arsenic resistance of CeO(2)–La(2)O(3)/TiO(2) catalyst for selective catalytic reduction of NO(x) with NH(3)
por: Wang, Na, et al.
Publicado: (2021)

Oxidative coupling of methane—comparisons of MnTiO(3)–Na(2)WO(4) and MnO(x)–TiO(2)–Na(2)WO(4) catalysts on different silica supports
por: Tiyatha, Worapinit, et al.
Publicado: (2022)

Ag Catalysts Supported on CeO(2), MnO(2) and CeMnO(x) Mixed Oxides for Selective Catalytic Reduction of NO by C(3)H(6)
por: La Greca, Eleonora, et al.
Publicado: (2023)

Effect of the valence state of Mn in MnO(x)/Ti(4)O(7) composites on the catalytic performance for oxygen reduction reaction and oxygen evolution reaction
por: Bai, Fan, et al.
Publicado: (2021)

Self-Organized TiO(2)–MnO(2) Nanotube Arrays for Efficient Photocatalytic Degradation of Toluene
por: Nevárez-Martínez, María C., et al.
Publicado: (2017)

Nano-MnO(2) Decoration of TiO(2) Microparticles to Promote Gaseous Ethanol Visible Photoremoval
por: Stucchi, Marta, et al.
Publicado: (2018)

Effects of SO(2) on selective catalytic reduction of NO with NH(3) over a TiO(2) photocatalyst
por: Yamamoto, Akira, et al.
Publicado: (2015)

A Cellulose-Derived Nanofibrous MnO(2)-TiO(2)-Carbon Composite as Anodic Material for Lithium-Ion Batteries
por: Li, Shun, et al.
Publicado: (2021)

High N(2) selectivity in selective catalytic reduction of NO with NH(3) over Mn/Ti–Zr catalysts
por: Zhang, Bolin, et al.
Publicado: (2018)

TiO(2)–SiO(2) supported MnWO(x) catalysts by liquid-phase deposition for low-temperature NH(3)-SCR
por: Lu, Weizhe, et al.
Publicado: (2019)

Revealing the crystal facet effect on N(2)O formation during the NH(3)-SCR over α-MnO(2) catalysts
por: Guo, Jundong, et al.
Publicado: (2023)

Improvement of O(2) adsorption for α-MnO(2) as an oxygen reduction catalyst by Zr(4+) doping
por: Wang, Yicheng, et al.
Publicado: (2018)

In Situ DRIFTS Studies of NH(3)-SCR Mechanism over V(2)O(5)-CeO(2)/TiO(2)-ZrO(2) Catalysts for Selective Catalytic Reduction of NO(x)
por: Zhang, Yaping, et al.
Publicado: (2018)

Comparison of CO(2) Reduction Performance with NH(3) and H(2)O between Cu/TiO(2) and Pd/TiO(2)
por: Nishimura, Akira, et al.
Publicado: (2021)

Annealing Strategies for the Improvement of Low-Temperature NH(3)-Selective Catalytic Reduction Activity of CrMnO(x) Catalysts
por: Zhang, Yanke, et al.
Publicado: (2019)

Preparation of Mesoporous Mn–Ce–Ti–O Aerogels by a One-Pot Sol–Gel Method for Selective Catalytic Reduction of NO with NH(3)
por: Wei, Yabin, et al.
Publicado: (2020)

Electrocatalytic Hydrogenation of N(2) to NH(3) by MnO: Experimental and Theoretical Investigations
por: Wang, Zao, et al.
Publicado: (2018)

Preparation of PEDOT/GO, PEDOT/MnO(2), and PEDOT/GO/MnO(2) nanocomposites and their application in catalytic degradation of methylene blue
por: Zhang, Li, et al.
Publicado: (2015)

Suppressed N(2)O formation during NH(3) selective catalytic reduction using vanadium on zeolitic microporous TiO(2)
por: Lee, Seung Gwan, et al.
Publicado: (2015)

Mixed Catalyst SmMn(2)O(5)/Cu-SAPO34 for NH(3)-Selective Catalytic Oxidation
por: Dong, Anqi, et al.
Publicado: (2022)

Enhanced Cycleability of Amorphous MnO(2) by Covering on α-MnO(2) Needles in an Electrochemical Capacitor
por: Liu, Quanbing, et al.
Publicado: (2017)

Comparative Studies of Effects of Vapor- and Liquid-Phase As(2)O(3) on Catalytic Behaviors of V(2)O(5)–WO(3)/TiO(2) Catalysts for NH(3)-SCR
por: Zhang, Handan, et al.
Publicado: (2020)

Cannot write session to /tmp/vufind_sessions/sess_jel2i03fn4t1m4ob3kj8eq66nr