Structural, magnetic, electrical and dielectric properties of Pr(0.8)Na(0.2)MnO(3) manganite

The orthorhombic Pr(0.8)Na(0.2)MnO(3) ceramic was prepared in polycrystalline form by a Pechini sol–gel method and its structural, magnetic, electrical and dielectric properties were investigated experimentally. A structural study confirms that the sample is single phase. Magnetic measurements show...

Descripción completa

Detalles Bibliográficos
Autores principales: Ouni, I., Ben Khlifa, H., M'nassri, R., Nofal, Muaffaq M., Rahmouni, H., Cheikhrouhou, W., Chniba-Boudjada, N., Khirouni, K., Cheikhrouhou, A.
Formato: Online Artículo Texto
Lenguaje:English
Publicado: The Royal Society of Chemistry 2019
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9074664/
https://www.ncbi.nlm.nih.gov/pubmed/35528058
http://dx.doi.org/10.1039/c9ra05414f
Descripción
Sumario:The orthorhombic Pr(0.8)Na(0.2)MnO(3) ceramic was prepared in polycrystalline form by a Pechini sol–gel method and its structural, magnetic, electrical and dielectric properties were investigated experimentally. A structural study confirms that the sample is single phase. Magnetic measurements show that the sample is a charge ordered manganite. The sample undergoes two successive magnetic phase transitions with the variation of temperature: a charge ordering transition occurred at T(CO) = 212 K followed by a paramagnetic (PM) to ferromagnetic (FM) transition around T(C) = 115 K. From an electrical point of view, a saturation region was marked in the conductivity as a function of temperature σ(T) curves at a specific temperature. The dc-conductivity (σ(dc)) reaches a maximum value at 240 K. The obtained results are in good agreement with the temperature dependence of the average normalized change (ANC). We found that the conduction mechanism was governed by small polaron hopping (SPH) in the high temperature region and by variable range hopping (VRH) in the low temperature region. Complex impedance analysis indicates the presence of a non-Debye relaxation phenomenon in the system. Also, the compound was modeled by an electrical equivalent circuit. Then, the contribution of the grain boundary in the transport properties was confirmed.