Axial Crystal Growth Evolution and Crystallization Characteristics of Bi-Continuous Polyamide 66 Membranes Prepared via the Cold Non-Solvent-Induced Phase Separation Technique

Polyamide 66 microporous membranes were prepared by cold non-solvent-induced phase separation using polyamide 66-formic acid-propylene carbonate as a ternary membrane-forming system. The formed membranes exhibited a special bicontinuous structure consisting of interglued spherical crystals or interlocked bundles of microcrystalline aggregates. The variation of the microporous structure under the influence of preparation conditions, solvent, aging time, and polymer concentration affects the comprehensive performance of the membranes. For example, the cold-induced operation and the use of different membrane-forming solvents contributed to the crystallization of polyamide 66, resulting in an increased contact angle of polyamide 66 membranes, obtaining a high resistance to contamination of up to 73.5%. Moreover, the formed membranes still have high mechanical strength.