Effect of Mechanical Shock Treatment on Microstructure and Corrosion Properties of Manual Argon Arc Welding Joints of 2205 Duplex Stainless Steel

Pneumatic chipping hammer and ultrasonic impact peening were used to relieve the welding residual stress of 2205 duplex stainless steel by manual argon arc welding, and the influences of these mechanical shock treatment technologies on the residual stress, microstructure, and corro-sion resistance of the welding seam were studied. Results showed that after pneumatic chipping hammer or ultrasonic impact peening, a small amount of plastic deformation occurred in the welded joint of 2205 duplex stainless steel, which led to an increase in the dislocation density in the microstructure. Meanwhile, the stress state of the welded joint changed from the residual tensile stress to the residual compressive stress. The maximum residual compressive stress could reach −579 MPa. The combined action of the two effectively improved the corrosion resistance of the welded joint. Among them, the best overall effect was the ultrasonic impact peening tech-nology.