Synthesis of (Hyper)Branched Monohydroxyl Alkoxysilane Oligomers toward Silanized Urethane Prepolymers

The aim of this work was the synthesis of (hyper)branched oligomers based on trialkoxysilane in various conditions and further application of them in order to modify the urethane prepolymers. Hydroxyl-terminated trialkoxysilane was used as a monomer for homo-condensation. It was obtained by reaction of 3-aminopropyl trialkoxysilane (APTES) with ethylene carbonate (EC). The reaction was based on the attack of amine at the carbonyl carbon atom followed by ring opening of the carbonate to give a urethane (carbamate) product. The next step was the condensation via substitution of ethoxy groups on silicon atom with the terminal hydroxyalkyl groups present in the primary product with the evolution of ethanol. Accordingly, the impact of temperature and type of catalyst on process efficiency was investigated. A quantitative analysis of reaction progress and products of the conversion of EC together with ethanol evolution was conducted by means of gas chromatography, which allowed us to determine the formation of monomeric product and, indirectly, of oligomeric products. It was found that at room temperature after 24 h, the majority of the monomeric product was isolated, whereas at elevated temperature in the presence of Ti-based catalyst, further condensation of the monomer into branched oligomers was preferred, and, moreover, the application of vacuum intensified that process. The obtained products were structurally characterized by (1)H and (29)Si NMR, MALDI-ToF and Gel Permeation Chromatography. Finally, two different alkoxysilane products, monomeric and oligomeric, were applied for modification of urethane prepolymer, forming silanized one (SPUR). The influence of the silanizing agent on the mechanical and thermal properties of the moisture-cured products was shown before and after additional conditioning in water.