The Modification of Poly(3-Hydroxybutyrate-co-4-hydroxybutyrate) by Melt Blending

Crystalline and noncrystalline poly(3-hyroxybutylate-co-4-hyroxybutylate) (P(3HB-co-4HB)) were melt blended to obtain mixtures of P(3HB-co-4HB) copolymers. The mixtures and P(3HB-co-4HB) copolymers of different 4HB contents were compared to study the effect of 4HB content on the properties of the copolymers and mixtures. P(3HB-co-4HB) copolymer mixtures, having various 4HB content, have been successfully made by melt blending instead of bacterial biosynthesis. In the case of copolymers, they were noncrystalline when the 4HB content was over 16%, while the P(3HB-co-4HB) mixtures at the same 4HB content were crystalline. The mixtures had a higher glass transition temperature, suggesting that their chain mobility is relatively low compared with the copolymer having the same 4HB content. Due to this effect, the mixture is expected to have a higher melt viscosity and a lower loss tangent to exhibit better melt processing properties. The mechanical properties of the mixtures show a similar behavior to the copolymers in that the tensile strength and the modulus decreases and elongation at the break increases with an increase in the 4HB content.