Study of the Influence of the Type of Aging on the Behavior of Delamination of Adhesive Joints in Carbon-Fiber-Reinforced Epoxy Composites

This study analyzes the behavior under the static delamination and mode-I fracture stress of adhesive joints made on the same composite material with an epoxy matrix and unidirectional carbon fiber reinforcement and two types of adhesives, one epoxy and the other acrylic. Standard DCB tests (for mode-I fracture) were used to quantify the influence on the interlaminar fracture toughness of the type of adhesive used. Both materials were subjected to two different degradation processes, one hygrothermal and the other in a salt-fog chamber. After aging, the mode-I fracture has been evaluated for both materials. From the experimental results obtained, it can be deduced for the epoxy adhesive that exposure to the hygrothermal environment used moderately modifies its behavior against delamination, while its exposure to the saline environment produces a significant loss of its resistance to delamination. For the acrylic adhesive, the hygrothermal exposure causes an improvement in its delamination behavior for all the exposure periods considered, while the saline environment slightly modifies its behavior. There is, therefore, a clear influence of the type of aging on the fracture behavior of both adhesives.