Morphological and Structural Transformations of Fe-Pd Powder Alloys Formed by Galvanic Replacement, Annealing and Acid Treatment

In this article, we report the preparation and structural features of Fe-Pd powder alloys formed by galvanic replacement, annealing and selective dissolution of iron via acid treatment. The alloys were studied by the X-ray diffraction phase analysis, Mössbauer spectroscopy, scanning electron microsc...

Descripción completa

Detalles Bibliográficos
Autores principales: Petrov, Sergey A., Dudina, Dina V., Ukhina, Arina V., Bokhonov, Boris B.
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2022
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9145926/
https://www.ncbi.nlm.nih.gov/pubmed/35629598
http://dx.doi.org/10.3390/ma15103571
Descripción
Sumario:In this article, we report the preparation and structural features of Fe-Pd powder alloys formed by galvanic replacement, annealing and selective dissolution of iron via acid treatment. The alloys were studied by the X-ray diffraction phase analysis, Mössbauer spectroscopy, scanning electron microscopy, and energy-dispersive spectroscopy. The Fe@Pd core–shell particles were obtained by a galvanic replacement reaction occurring upon treatment of a body-centered cubic (bcc) iron powder by a solution containing PdCl(4)(2−) ions. It was found that the shells are a face-centered cubic (fcc) Pd(Fe) solid solution. HCl acid treatment of the Fe@Pd core–shell particles resulted in the formation of hollow Pd-based particles, as the bcc phase was selectively dissolved from the cores. Annealing of the Fe@Pd core–shell particles at 800 °C led to the formation of fcc Fe-Pd solid solution. Acid treatment of the Fe-Pd alloys formed by annealing of the core–shell particles allowed selectively dissolving iron from the bcc Fe-based phase (Fe(Pd) solid solution), while the fcc Fe-rich Fe-Pd solid solution remained stable (resistant to acid corrosion). It was demonstrated that the phase composition and the Fe/Pd ratio in the alloys (phases) can be tailored by applying annealing and/or acid treatment to the as-synthesized Fe@Pd core–shell particles.