Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy

Ultrasonic treatment was applied to an A356 aluminum melt with different modifiers, and the effects of ultrasonic treatment on the structure and properties of the A356 alloy were studied. The results showed that α-Al was effectively refined with different ultrasonic modification treatments. In parti...

Descripción completa

Detalles Bibliográficos
Autores principales: Hu, Xinyi, Song, Dongfu, Wang, Huiping, Jia, Yiwang, Zou, Haiping, Chen, Mingjuan
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2022
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9147325/
https://www.ncbi.nlm.nih.gov/pubmed/35629740
http://dx.doi.org/10.3390/ma15103714
_version_ 1784716779729190912
author Hu, Xinyi
Song, Dongfu
Wang, Huiping
Jia, Yiwang
Zou, Haiping
Chen, Mingjuan
author_facet Hu, Xinyi
Song, Dongfu
Wang, Huiping
Jia, Yiwang
Zou, Haiping
Chen, Mingjuan
author_sort Hu, Xinyi
collection PubMed
description Ultrasonic treatment was applied to an A356 aluminum melt with different modifiers, and the effects of ultrasonic treatment on the structure and properties of the A356 alloy were studied. The results showed that α-Al was effectively refined with different ultrasonic modification treatments. In particular, ultrasonic treatment showed the most obvious refinement with macroscopic grains of unmodified alloy and optimized the refinement of secondary dendrite arm spacings in the Sr/Ce synergistic alloys. The eutectic Si of the unmodified A356 alloy had no obvious change after the ultrasonic treatment, but the branch diameter of the eutectic Si reduced in the Sr and Sr/Ce modification alloys after the ultrasonic treatment. The ultrasonic treatment significantly improved the ultimate tensile strength and elongation of the as-cast A356 alloy with the unmodified material, which was due to refinement of the α-Al grains by the ultrasonic treatment. After the T6 heat treatment, the ultimate tensile strength values of the alloys showed no obvious change due to the ultrasonic treatment, but the plasticity of the alloy was significantly improved. Mg(2)Si precipitation was the dominant strengthening mechanism during the T6 heat treatment, while the plasticity was determined by the size and distribution of the eutectic Si. Acoustic cavitation caused by the ultrasound-activated impurities and the induced heterogeneous nucleation and supercooled nucleation in the groove melt was the main cause of the α-Al refinement, the eutectic Si modification and the improvement in the mechanical properties.
format Online
Article
Text
id pubmed-9147325
institution National Center for Biotechnology Information
language English
publishDate 2022
publisher MDPI
record_format MEDLINE/PubMed
spelling pubmed-91473252022-05-29 Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy Hu, Xinyi Song, Dongfu Wang, Huiping Jia, Yiwang Zou, Haiping Chen, Mingjuan Materials (Basel) Article Ultrasonic treatment was applied to an A356 aluminum melt with different modifiers, and the effects of ultrasonic treatment on the structure and properties of the A356 alloy were studied. The results showed that α-Al was effectively refined with different ultrasonic modification treatments. In particular, ultrasonic treatment showed the most obvious refinement with macroscopic grains of unmodified alloy and optimized the refinement of secondary dendrite arm spacings in the Sr/Ce synergistic alloys. The eutectic Si of the unmodified A356 alloy had no obvious change after the ultrasonic treatment, but the branch diameter of the eutectic Si reduced in the Sr and Sr/Ce modification alloys after the ultrasonic treatment. The ultrasonic treatment significantly improved the ultimate tensile strength and elongation of the as-cast A356 alloy with the unmodified material, which was due to refinement of the α-Al grains by the ultrasonic treatment. After the T6 heat treatment, the ultimate tensile strength values of the alloys showed no obvious change due to the ultrasonic treatment, but the plasticity of the alloy was significantly improved. Mg(2)Si precipitation was the dominant strengthening mechanism during the T6 heat treatment, while the plasticity was determined by the size and distribution of the eutectic Si. Acoustic cavitation caused by the ultrasound-activated impurities and the induced heterogeneous nucleation and supercooled nucleation in the groove melt was the main cause of the α-Al refinement, the eutectic Si modification and the improvement in the mechanical properties. MDPI 2022-05-22 /pmc/articles/PMC9147325/ /pubmed/35629740 http://dx.doi.org/10.3390/ma15103714 Text en © 2022 by the authors. https://creativecommons.org/licenses/by/4.0/Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/).
spellingShingle Article
Hu, Xinyi
Song, Dongfu
Wang, Huiping
Jia, Yiwang
Zou, Haiping
Chen, Mingjuan
Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy
title Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy
title_full Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy
title_fullStr Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy
title_full_unstemmed Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy
title_short Effect of Ultrasonic-Assisted Modification Treatment on the Microstructure and Properties of A356 Alloy
title_sort effect of ultrasonic-assisted modification treatment on the microstructure and properties of a356 alloy
topic Article
url https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9147325/
https://www.ncbi.nlm.nih.gov/pubmed/35629740
http://dx.doi.org/10.3390/ma15103714
work_keys_str_mv AT huxinyi effectofultrasonicassistedmodificationtreatmentonthemicrostructureandpropertiesofa356alloy
AT songdongfu effectofultrasonicassistedmodificationtreatmentonthemicrostructureandpropertiesofa356alloy
AT wanghuiping effectofultrasonicassistedmodificationtreatmentonthemicrostructureandpropertiesofa356alloy
AT jiayiwang effectofultrasonicassistedmodificationtreatmentonthemicrostructureandpropertiesofa356alloy
AT zouhaiping effectofultrasonicassistedmodificationtreatmentonthemicrostructureandpropertiesofa356alloy
AT chenmingjuan effectofultrasonicassistedmodificationtreatmentonthemicrostructureandpropertiesofa356alloy