Experimental Study on the Mechanical Properties, Water Absorption, and Fiber Degradation of Naturally Aged Glass Fiber and Polypropylene Fiber-Reinforced Concrete

The main objective of this study is to better understand the performance changes of naturally aged glass fiber-reinforced concrete (GFRC) and polypropylene fiber-reinforced concrete (PPFRC), especially the degradation of fibers, which is of great significance for evaluating the durability of structures using these two types of composite materials. The mechanical properties, water absorption, and microstructures of GFRC and PPFRC at a curing age of three years, including their compressive strength, full curves of water absorption, fiber-matrix interaction, and fiber degradation, were systematically studied, and the related properties were compared with those at the curing age of 28 days. The degradation of fibers after freeze-thaw cycles was also studied. The results revealed the following. The water/binder ratio (w/b) affects the rate of increase of the long-term compressive strength of naturally aged concrete. In general, the water absorption of fiber-reinforced concrete (FRC) at the curing age of three years was found to be significantly reduced, but with the increases of w/b and the fiber content to the maximum values, the water absorption of the specimens cured for three years was higher than that of the specimens cured for 28 days. Moreover, with the increase of the curing age, the optimal glass fiber (GF) contents for reducing the water absorption decreased from 1.35% to 0.90% (w/b = 0.30), and from 0.90% to 0.45% (w/b = 0.35), respectively. The GF surface was degraded into continuous pits with diameters of about 200 to 600 nm, and the surface of the pits was attached with spherical granular C-S-H gel products with diameters of about 30 to 44 nm. The freeze-thaw cycles were found to have no significant effect on the pits on the GF surface and the granular C-S-H gel products attached to the pits, but caused a portion of the cement matrix covering the GF to fall off. The interfacial bonding between the polypropylene fiber (PPF) and the cement matrix exhibited almost no change in the PPFRC after three years of curing as compared with that after 28 days of curing. Furthermore, the cement hydration gel on the PPF surface was not significantly damaged by 150 freeze-thaw cycles.