Remineralization of early enamel lesions with a novel prepared tricalcium silicate paste

To evaluate the remineralization potential of prepared tricalcium silicate (TCS) paste compared to silver diamine fluoride-potassium iodide (SDF-KI) and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on artificial enamel lesions. Thirty permanent sound molars were collected for the study. After cleaning, root cutting, and applying acid-resistant nail varnish, leaving a 4 × 4 mm buccal window, the teeth were subjected to demineralization process. The teeth were divided into three treatment groups (n = 10). In each group, the teeth were sectioned buccolingually to obtain two halves (30 self-control and 30 experimental halves). The self-control halves were subjected to cross-sectional microhardness (CSMH), energy-dispersive X-ray spectroscopy at 50, 100, and 150 µm from the external enamel surface, and micromorphological analysis at the superficial enamel surface. The experimental halves were subjected to the same tests after 30 days of remineralization. Three-way analysis of variance (ANOVA) outcomes showed no significant difference in CSMH after treatment among the three different groups at the different levels (p > 0.05). Meanwhile, three-way ANOVA outcomes showed a significant difference in calcium/ phosphate ratio after treatment among the three different groups at the different levels. (p < 0.05). The tricalcium silicate paste used in this study showed potential remineralization in subsurface enamel lesions.