High-Temperature Tribological Behavior of HDPE Composites Reinforced by Short Carbon Fiber under Water-Lubricated Conditions

The polymer water-lubricated bearing is widely used in marine transmission systems, and the tribological properties can be improved by addition of inorganic nano-fillers. The aim of this study is to investigate the effect of SCFs and temperature on the water-lubricating properties of high-density polyethylene (HDPE) composites. HDPE composites reinforced by varying content of short carbon fibers (SCFs) were fabricated via twin-screw extrusion and injection molding techniques to study the hardness and surface wettability of those composites. The tribological properties under water-lubricated conditions were investigated through a pin-on-disk reciprocating tribometer under different temperatures. The results showed that the increase in hardness of HDPE composites reached maximum to 42.9% after adding 25 wt % SCFs. The contact angle also increased with the increase in SCFs content and reached a maximum of 95.2° as the amount of SCFs increased to 20 wt %. The incorporation of SCFs increased the wear resistance and lubricating property of HDPE composites at different temperatures. The HDPE composite containing 20 wt % SCFs showed the lowest friction coefficient of 0.076 at 40 °C, and the wear track depth reached a maximum of 36.3 mm at 60 °C. Based on the surface wetting property and wear analysis, potential effect mechanisms of fillers and temperature were discussed. The knowledge from this study is useful for designing the anti-wear water-lubricated polymer bearing.