Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems
Objectives: The aim of this study was to assess the microtensile bond strength of three universal adhesives to dentin and enamel. Materials and Methods: Sixty extracted human third molar teeth were chosen and divided into six groups regarding the adhesive (G-Premio Bond, Clearfil S3 Bond or Single B...
Autores principales: | , , , , , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Tehran University of Medical Sciences
2022
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9294723/ https://www.ncbi.nlm.nih.gov/pubmed/35937153 http://dx.doi.org/10.18502/fid.v19i8.8725 |
_version_ | 1784749904252370944 |
---|---|
author | Jafarnia, Shiva Zeinaddini Meymand, Javad Zandkarimi, Fateme Saberi, Sogol Shahabi, Sima Valanezhad, Alireza Safaee, Sirus Nesabi, Mahdis Watanabe, Ikuya |
author_facet | Jafarnia, Shiva Zeinaddini Meymand, Javad Zandkarimi, Fateme Saberi, Sogol Shahabi, Sima Valanezhad, Alireza Safaee, Sirus Nesabi, Mahdis Watanabe, Ikuya |
author_sort | Jafarnia, Shiva |
collection | PubMed |
description | Objectives: The aim of this study was to assess the microtensile bond strength of three universal adhesives to dentin and enamel. Materials and Methods: Sixty extracted human third molar teeth were chosen and divided into six groups regarding the adhesive (G-Premio Bond, Clearfil S3 Bond or Single Bond) and tooth surface. All the applied bonding agents were universal adhesives. The teeth were polished and the adhesives were applied; then the teeth were restored with composite resin. The samples were mounted in acrylic resin and sectioned. The specimens were subjected to a universal testing machine and the microtensile bond strength was measured. The failure mode of each specimen was determined under a stereomicroscope. Data were analyzed using two-way ANOVA (α=0.05). Results: The microtensile bond strength of G-Premio Bond to enamel and dentin was 11.79±8.27 and 17.55±9.47 MPa, respectively which was not significantly different from the values in Single Bond group (15.59±10.66 and 17.19±10.09 MPa to enamel and dentin, respectively; P>0.05). However, the values for Clearfil S3 Bond were 7.11±4.23 and 7.88±8.83 MPa to enamel and dentin, respectively, which were significantly lower than the values for G-Premio Bond (P<0.05). Scanning electron microscopic (SEM) images showed that the adhesive failure was dominant in both enamel and dentin groups and in all adhesive systems. Conclusion: G-Premio Bond and Single Bond provided higher microtensile bond strength compared with Clearfil S3 Bond. Universal adhesives with their acceptable performance can be applied in self-etch mode on both enamel and dentin. |
format | Online Article Text |
id | pubmed-9294723 |
institution | National Center for Biotechnology Information |
language | English |
publishDate | 2022 |
publisher | Tehran University of Medical Sciences |
record_format | MEDLINE/PubMed |
spelling | pubmed-92947232022-08-04 Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems Jafarnia, Shiva Zeinaddini Meymand, Javad Zandkarimi, Fateme Saberi, Sogol Shahabi, Sima Valanezhad, Alireza Safaee, Sirus Nesabi, Mahdis Watanabe, Ikuya Front Dent Original Article Objectives: The aim of this study was to assess the microtensile bond strength of three universal adhesives to dentin and enamel. Materials and Methods: Sixty extracted human third molar teeth were chosen and divided into six groups regarding the adhesive (G-Premio Bond, Clearfil S3 Bond or Single Bond) and tooth surface. All the applied bonding agents were universal adhesives. The teeth were polished and the adhesives were applied; then the teeth were restored with composite resin. The samples were mounted in acrylic resin and sectioned. The specimens were subjected to a universal testing machine and the microtensile bond strength was measured. The failure mode of each specimen was determined under a stereomicroscope. Data were analyzed using two-way ANOVA (α=0.05). Results: The microtensile bond strength of G-Premio Bond to enamel and dentin was 11.79±8.27 and 17.55±9.47 MPa, respectively which was not significantly different from the values in Single Bond group (15.59±10.66 and 17.19±10.09 MPa to enamel and dentin, respectively; P>0.05). However, the values for Clearfil S3 Bond were 7.11±4.23 and 7.88±8.83 MPa to enamel and dentin, respectively, which were significantly lower than the values for G-Premio Bond (P<0.05). Scanning electron microscopic (SEM) images showed that the adhesive failure was dominant in both enamel and dentin groups and in all adhesive systems. Conclusion: G-Premio Bond and Single Bond provided higher microtensile bond strength compared with Clearfil S3 Bond. Universal adhesives with their acceptable performance can be applied in self-etch mode on both enamel and dentin. Tehran University of Medical Sciences 2022-02-06 /pmc/articles/PMC9294723/ /pubmed/35937153 http://dx.doi.org/10.18502/fid.v19i8.8725 Text en Copyright © 2022 The Authors. Published by Tehran University of Medical Sciences. https://creativecommons.org/licenses/by-nc/4.0/This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International license (https://creativecommons.org/licenses/by-nc/4.0/). Non-commercial uses of the work are permitted, provided the original work is properly cited. |
spellingShingle | Original Article Jafarnia, Shiva Zeinaddini Meymand, Javad Zandkarimi, Fateme Saberi, Sogol Shahabi, Sima Valanezhad, Alireza Safaee, Sirus Nesabi, Mahdis Watanabe, Ikuya Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems |
title | Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems |
title_full | Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems |
title_fullStr | Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems |
title_full_unstemmed | Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems |
title_short | Comparative Evaluation of Microtensile Bond Strength of Three Adhesive Systems |
title_sort | comparative evaluation of microtensile bond strength of three adhesive systems |
topic | Original Article |
url | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9294723/ https://www.ncbi.nlm.nih.gov/pubmed/35937153 http://dx.doi.org/10.18502/fid.v19i8.8725 |
work_keys_str_mv | AT jafarniashiva comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT zeinaddinimeymandjavad comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT zandkarimifateme comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT saberisogol comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT shahabisima comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT valanezhadalireza comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT safaeesirus comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT nesabimahdis comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems AT watanabeikuya comparativeevaluationofmicrotensilebondstrengthofthreeadhesivesystems |