Comparative Evaluation of Microleakage of Flowable Composite Resin Using Etch and Rinse, Self-Etch Adhesive Systems, and Self-Adhesive Flowable Composite Resin in Class V Cavities: Confocal Laser Microscopic Study

The essential factor in determining the preservation of restoration is the marginal seal. Restoring cervical lesions with a resin composite has always been a challenge. Composite resins with various viscosities and different bonding systems are being researched to reduce the microleakage. Confocal l...

Descripción completa

Detalles Bibliográficos
Autores principales: Sengar, Ekta Varma, Mulay, Sanjyot, Beri, Lotika, Gupta, Archana, Almohareb, Thamer, Binalrimal, Sultan, Robaian, Ali, Bahammam, Maha A., Bahammam, Hammam Ahmed, Bahammam, Sarah Ahmed, Zidane, Bassam, Albar, Nassreen H., Bhandi, Shilpa, Shrivastava, Deepti, Srivastava, Kumar Chandan, Patil, Shankargouda
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2022
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9319247/
https://www.ncbi.nlm.nih.gov/pubmed/35888429
http://dx.doi.org/10.3390/ma15144963
Descripción
Sumario:The essential factor in determining the preservation of restoration is the marginal seal. Restoring cervical lesions with a resin composite has always been a challenge. Composite resins with various viscosities and different bonding systems are being researched to reduce the microleakage. Confocal laser scanning microscopy (CLSM) is the latest non-destructive technique for visualizing the microleakage. Objectives: To evaluate and compare the microleakage of Universal Flo composite resin (G-aenial) using etch and rinse adhesive system ER-2 steps (Adper Single Bond 2), self-etch adhesive system SE-1 step (G-Bond), and self-adhesive flowable composite resin (Constic) in Class V cavities using a confocal laser scanning microscope. Materials and Method: Class V cavities were prepared on 27 caries-free human extracted premolar teeth on the buccal and lingual surfaces with standardized dimensions of 2 mm height, width 4 mm, and a depth of 2 mm. After the cavity preparation, all teeth were randomly divided into three groups, namely Group-I: G-aenial Universal Flo with Single Bond 2 (n = 9 teeth); Group-II: G- aenial Universal Flo with G-Bond (n = 9 teeth), and Group-III: Constic (n = 9 teeth). The prepared and restored specimens were then subjected to thermocycling for 500 cycles in a water bath at 5 °C and 55 °C with a dwelling time of 30 s. The specimens were placed in 0.6% aqueous rhodamine dye for 48 h. Sectioning was carried out bucco-lingually and specimens were evaluated for microleakage under a confocal laser scanning microscope. Results: There was a significant difference (p = 0.009) in microleakage when comparing total etch and rinse, specifically between Adper Single Bond 2 ER-2 steps (fifth generation) and self-adhesive flowable composite resin, which is Constic. There was more microleakage in the self-etch bonding agent, particularly G-Bond, SE-1 step (seventh generation), when compared to ER-2 steps (fifth generation bonding agent); however, the results were not statistically significant (p = 0.468). The self-adhesive flowable composite resin showed more microleakage than SE-1 step and ER-2 steps. Conclusions: None of the adhesive systems tested were free from microleakage. However, less microleakage was observed in the total etch and rinse, especially Adper Single Bond 2 (ER-2 steps), than the self-etch adhesive system SE-1 step and self-adhesive flowable composite resin. Clinical significance: Constant research and technological advancements are taking place in dentin adhesives to improve the marginal seal. This has led to the evolution of total acid-etching dentin bonding agents termed as etch and rinse (ER)-2 steps (fifth generation dentin bonding agents) and self-etching (SE) 2 steps, and SE-1 step dentin bonding agents termed as the sixth and seventh generation bonding agents, respectively.