Experimental Research on Fatigue Crack Growth Behavior of Diffusion-Bonded Titanium Alloy Laminates with Preset Unbonded Areas

This paper aimed to study the fatigue crack growth behavior of diffusion-bonded titanium alloy laminates (DB-TAL) with preset unbonded areas using an experimental method to understand the toughening mechanisms of presetting unbonded areas in DB-TAL. For two series of specimens of DB-TAL with preset unbonded areas with an open hole, which have a pre-notch at the open hole edge, fatigue experiments under tension–tension cyclic loading were conducted. The fatigue crack growth process, the crack growth rate, and the stress intensity factor on the crack front were analyzed. The results showed that the preset unbonded area leads the crack away from the stress concentration zone and slows down the crack growth rate. Therefore, the preset unbonded area significantly improved the fracture property of DB-TAL.