Quasi-Solid-State Lithium-Sulfur Batteries Assembled by Composite Polymer Electrolyte and Nitrogen Doped Porous Carbon Fiber Composite Cathode

Solid-state lithium sulfur batteries are becoming a breakthrough technology for energy storage systems due to their low cost of sulfur, high energy density and high level of safety. However, its commercial application has been limited by the poor ionic conductivity and sulfur shuttle effect. In this paper, a nitrogen-doped porous carbon fiber (NPCNF) active material was prepared by template method as a sulfur-host of the positive sulfur electrode. The morphology was nano fiber-like and enabled high sulfur content (62.9 wt%). A solid electrolyte membrane (PVDF/LiClO(4)/LATP) containing polyvinylidene fluoride (PVDF) and lithium aluminum titanium phosphate (Li(1).(3)Al(0).(3)Ti(1).(7)(PO(4))(3)) was prepared by pouring and the thermosetting method. The ionic conductivity of PVDF/LiClO4/LATP was 8.07 × 10(−5) S cm(−1) at 25 °C. The assembled battery showed good electrochemical performance. At 25 °C and 0.5 C, the first discharge specific capacity was 620.52 mAh g(−1). After 500 cycles, the capacity decay rate of each cycle was only 0.139%. The synergistic effect between the composite solid electrolyte and the nitrogen-doped porous carbon fiber composite sulfur anode studied in this paper may reveal new approaches for improving the cycling performance of a solid-state lithium-sulfur battery.