Experimental Research on Mechanical and Shrinkage Properties of Alkali Activated Low-Carbon Green Concrete

This paper describes orthogonal experiments to investigat the effects of content of fly ash and slag, sol ratio, modulus of sodium silicate and expander on the compressive strength and shrinkage of alkali activated low-carbon green concrete (AAGC) of different ages. The microstructures and hydration product compositions of AAGC with different proportions were further studied by Scanning Electron Microscopy (SEM), X-ray Diffraction (XRD) and Mercury Intrusion Porosimetry (MIP). The results show that with an increase of fly ash content, the compressive strength of AAGC gradually decreases, the decline of compressive strength at 28 d is smaller than that of 7 d, and the shrinkage strain gradually increases at 28 d. As the sol ratio increases, the compressive strength increases first and then decreases. When the sol ratio is 0.42, the compressive strength is maximal at 28 d; the same is true for compressive strength at 7 d. Additionally, an increase of sol ratio can reduce the shrinkage strain at 28 d. Finally, when the sol ratio was 0.46, the shrinkage decreased by 30.5% compared with 0.40 at 28 d. As the modulus of sodium silicate (M(s)) increases, the compressive strength first increases and then decreases. When M(s) is 1.4, the compressive strength reaches the maximum. As M(s) increases, the shrinkage strain decreases first and then increases at 28 d. When M(s) is 1.0, the shrinkage strain is the maximum at 28 d. Finally, with an increase in the content of expander, the compressive strength decreases at 7 d and 28 d, and the shrinkage strain decreases at 28 d. The shrinkage strain at 28 d is the minimum with 9% content. AAGC mixed with a small amount of fly ash and expander has more hydration products and significantly reduced cracks. In addition, the proportion of small hole volume of AAGC increases, while the proportion of large hole volume decreases. AAGC mixed with fly ash and slag without expander has more unhydrated particles and its structure is loose.