Early Spalling Analysis of Large Particles in High-Cr Steel during Thermal Fatigue: Relevant Mechanisms
The aim of this study was to investigate the surface deterioration of high-Cr roll steel caused by the spalling of larger particles during thermal fatigue. The mechanisms of surface deterioration due to spalling of larger particles are discussed. Using a laboratory thermal fatigue test that replicat...