Large-scale synthesis of mixed valence K(3)[Fe(2)S(4)] with high dielectric and ferrimagnetic characteristics

High yields of phase-pure K(3)[Fe(2)S(4)] are obtained using a fast, straight-forward, and efficient synthetic technique starting from the binary precursors K(2)S and FeS, and elemental sulphur. The compound indicates soft ferrimagnetic characteristics with magnetization of 15.23 A m(2) kg(−1) at 300 K due to the mixed valence of Fe(II)/Fe(III). Sintering at different temperatures allows the manipulation of the microstructure as well as the ratio of grains to grain boundaries. This results in a variation of dielectric and impedance properties. Samples sintered at 923 K demonstrate a dielectric constant (κ) of around 1750 at 1 kHz, which lies within the range of well-known high-κ dielectric materials, and an ionic conductivity of 4 × 10(−2) mS cm(−1) at room temperature. The compound has an optical band gap of around 2.0 eV, in agreement with tailored quantum chemical calculations. These results highlight its potential as a material comprising non-toxic and abundant elements for electronic and magnetic applications.