Marginal Misfit of 3D-Printed (Selective Laser Sintered), CAD-CAM and Lost Wax Technique Cobalt Chromium Copings with Shoulder and Chamfer Finish Lines: An In-Vitro Study

Background and Objectives: The aim was to compare the Misfit of 3D-Printed, Selective laser melting (SLM), milled (Computer aided design-Computer aided manufacture CAD-CAM) and Lost wax technique (LWT) fabricated Cobalt chromium (CoCr) alloy copings on shoulder (SH), radial shoulder (R-SH) and chamfer (CH) finish line configuration. Materials and Methods: Ninety resin, second maxillary premolar teeth were prepared for metal-ceramic crowns, equally divided into (n = 30) SH, R-SH and CH margin preparations. For each preparation design (SH, R-SH and CH), CoCr copings were prepared using SLM, CAD-CAM and LWT. This resulted in nine study groups with 10 CoCr copings each. The marginal misfit of specimens was assessed with a high-resolution digital microscope. Misfit was evaluated in vertical and horizontal dimensions in μm. Data were analyzed using ANOVA and a post hoc multiple comparisons test. Results: For vertical misfit, the highest was observed in SLM samples with chamfer margin (167.96 ± 24.1), and the least was shown by CAD-CAM samples with radial shoulder (58.8 ± 12.53). CAD-CAM and shoulder margins showed the least vertical misfit. For horizontal misfit, the maximum was observed in SLM samples with shoulder margin (137.94 ± 37.85) and the least by LWT samples with chamfer (89.38 ± 14.81). Chamfer margins and LWT samples showed the least horizontal misfit among the group samples. Fabrication technique and finish line design play a critical role in reducing the marginal misfit of CoCr copings. Conclusions: For vertical misfit, SLM copings showed poor outcomes compared to CAD-CAM specimens, however comparable outcomes to Cast specimens. SLM copings showed comparable horizontal misfit outcomes to CAD-CAM specimens and low misfit compared to Cast copings, respectively. Vertical misfit was low with shoulder margins, and horizontal misfit was better with chamfer marginal configuration.