Does ultrasonic activation improve the bond strength and root canal filling quality of endodontic sealers?

This study aimed to investigate the effect of ultrasonic activation (UA) of three endodontic sealers on the bond strength to root dentin and root canal filling quality. Ninety six bovine incisors were instrumented and root canal filling was carried out using AH Plus (AP), Sealer Plus (SP), or Sealer Plus BC (BC), with or without UA (n=16/group). Two 1.5-mm slices were obtained from each root third. The first slice was subjected to push-out testing and failure mode analysis, while the second was observed under a stereomicroscope for filling quality assessment. Data were analyzed by Kruskal-Wallis, Mann-Whitney and Friedman tests (α=0.05). SP showed higher bond strength and fewer voids than BC in the apical third and when root thirds data were pooled. SP also had higher bond strength compared with AH Plus in the apical third. UA improved the bond strength when BC was used but did not affect the filling quality of any sealer. There were no significant differences between the ultrasonically activated sealers regarding bond strength and filling quality. When root thirds were compared, the bond strength was similar along the root, but there was a tendency to worsen filling quality, with more voids, in the apical segment. In conclusion, UA was effective in increasing the bond strength of the calcium silicate-based sealer but did not improve its filling quality. For the epoxy resin-based sealers, these properties were not affected by UA.