A Novel Diamine Containing Ester and Diphenylethane Groups for Colorless Polyimide with a Low Dielectric Constant and Low Water Absorption
In this study, a novel diamine monomer containing ester and phenyl moieties, 1,2-diphenylethane-1,2-diyl bis(4-aminobenzoate) (1,2-DPEDBA), was synthesized through a three-step reaction. Using this diamine, a novel polyimide (PI) film was prepared with 4,4′-(hexafluoroisopropylidene)diphthalic anhyd...
Autores principales: | , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2022
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9657050/ https://www.ncbi.nlm.nih.gov/pubmed/36365498 http://dx.doi.org/10.3390/polym14214504 |
Sumario: | In this study, a novel diamine monomer containing ester and phenyl moieties, 1,2-diphenylethane-1,2-diyl bis(4-aminobenzoate) (1,2-DPEDBA), was synthesized through a three-step reaction. Using this diamine, a novel polyimide (PI) film was prepared with 4,4′-(hexafluoroisopropylidene)diphthalic anhydride (6-FDA) as a counter dianhydride through a typical two-step chemical imidization. For comparison, poly(pyromellitic dianhydride-co-4,4′-oxydianiline) (PMDA-ODA PI) was also synthesized via thermal imidization. The resulting 6-FDA-DPEDBA PI film was not only soluble in common polar solvents with high boiling points, such as N,N-dimethylacetamide (DMAc) and N,N-dimethylformamide (DMF), but also soluble in common low-boiling-point polar solvents, such as chloroform (CHCl(3)) and dichloromethane (CH(2)Cl(2)), at room temperature. The resulting novel PI showed a 5% weight loss temperature (T(5)(d)) at 360 °C under a nitrogen atmosphere. The resulting PI film was colorless and transparent with a transmittance of 87.1% in the visible light region ranging from 400 to 760 nm. The water absorption of the novel PI film was of 1.78%. The PI film also possessed a good moisture barrier and hydrophobicity. Furthermore, the resulting PI film displayed a low dielectric constant of 2.17 at 10(6) Hz at room temperature. In conclusion, the novel PI film exhibited much better optical transparency, lower moisture absorption, and a lower dielectric constant as well as better solubility than the PMDA-ODA PI film, which is insoluble in any solvent, although its thermal stability is not better than that of PMDA-ODA PI. |
---|