Postproduction Approach to Enhance the External Quantum Efficiency for Red Light-Emitting Diodes Based on Silicon Nanocrystals

Despite bulk crystals of silicon (Si) being indirect bandgap semiconductors, their quantum dots (QDs) exhibit the superior photoluminescence (PL) properties including high quantum yield (PLQY > 50%) and spectral tunability in a broad wavelength range. Nevertheless, their low optical absorbance character inhibits the bright emission from the SiQDs for phosphor-type light emitting diodes (LEDs). In contrast, a strong electroluminescence is potentially given by serving SiQDs as an emissive layer of current-driven LEDs with (Si-QLEDs) because the charged carriers are supplied from electrodes unlike absorption of light. Herein, we report that the external quantum efficiency (EQE) of Si-QLED was enhanced up to 12.2% by postproduction effect which induced by continuously applied voltage at 5 V for 9 h. The active layer consisted of SiQDs with a diameter of 2.0 nm. Observation of the cross-section of the multilayer QLEDs device revealed that the interparticle distance between adjacent SiQDs in the emissive layer is reduced to 0.95 nm from 1.54 nm by “post-electric-annealing”. The shortened distance was effective in promoting charge injection into the emission layer, leading improvement of the EQE.