Calcium Sulfate and Calcium Carbonate Scaling of Thin-Film Composite Polyamide Reverse Osmosis Membranes with Surface-Tethered Polyacrylic Acid Chains

The gypsum and calcite scaling propensities of the thin-film composite polyamide (PA-TFC) reverse osmosis (RO) membrane, modified with a tethered surface layer of polyacrylic acid (PAA) chains, was evaluated and compared to the scaling of selected commercial RO membranes. The tethered PAA layer was synthesized onto a commercial polyamide membrane (i.e., base-PA) via atmospheric pressure plasma-induced graft polymerization (APPIGP). The PAA nano-structured (SNS) base-PA membrane (SNS-PAA-PA) was scaled to a lesser degree, as quantified by a lower permeate flux decline and surface imaging, relative to the tested commercial membranes (Dow SW30, Toray SWRO, and BWRO). The cleaning of gypsum-scaled membranes with D.I. water flushing achieved 100% water permeability recovery for both the SNS-PAA-PA and Dow SW30 membranes, relative to 92–98% permeability restoration for the Toray membranes. The calcium carbonate scaling of SNS-PAA-PA membranes was also lower relative to the commercial membranes, but permeability recovery after D.I. water cleaning was somewhat lower (94%) but consistent with the level of surface scale coverage. In contrast, the calcite and gypsum-scaled membrane areas of the commercial membranes post-cleaning were significantly higher than for the SNS-PAA-PA membrane but with 100% permeability recovery, suggesting the potential for membrane damage when mineral scaling is severe.