Influence of Structural Characterization of C(3)S-C(3)A Paste under Sulfate Attack
The durability of C(3)S-C(3)A paste with varied C(3)A content (0%, 5%, 10%, and 20%) against sulfate attack at various attack ages (3 d, 7 d, 28 d, and 180 d) was investigated in this study through the examinations of corrosion product composition, Ca/Si and Al/Si of calcium-(aluminum)-silicate-hydr...
Autores principales: | Zhao, Qicai, He, Tao, Zhang, Gaozhan, Li, Yang, Rong, Guocheng, Ding, Qingjun |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2022
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9821662/ https://www.ncbi.nlm.nih.gov/pubmed/36614415 http://dx.doi.org/10.3390/ma16010077 |
Ejemplares similares
-
Effect of Layered Double Hydroxides on the Deterioration Process of Cement Paste under Sulfate Attack
por: Zhang, Lei, et al.
Publicado: (2022) -
Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack
por: Metalssi, Othman Omikrine, et al.
Publicado: (2023) -
The Mechanical Properties of Early Aged Shotcrete under Internal Sulfate Attack
por: Jin, Xiaoguang, et al.
Publicado: (2021) -
Study on the Deterioration of Concrete under Dry–Wet Cycle and Sulfate Attack
por: Liu, Fang, et al.
Publicado: (2020) -
Resistance of Pastes from Carbonated, Low-Lime Calcium Silica Cements to External Sulfate Attack †
por: Tokpatayeva, Raikhan, et al.
Publicado: (2023)