Characteristic and Mechanistic Investigation of Stress-Assisted Microbiologically Influenced Corrosion of X80 Steel in Near-Neutral Solutions

The behavior and mechanisms of the stress-assisted microbiologically influenced corrosion (MIC) of X80 pipeline steel induced by sulfate-reducing bacteria (SRB) were investigated using focused ion beam-scanning electron microscopy (FIB). Electrochemical results show that SRB and stress have a synerg...

Descripción completa

Detalles Bibliográficos
Autores principales:	Guo, Huihua, Zhong, Rui, Liu, Bo, Yang, Jike, Liu, Zhiyong, Du, Cuiwei, Li, Xiaogang
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2022
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9822082/ https://www.ncbi.nlm.nih.gov/pubmed/36614728 http://dx.doi.org/10.3390/ma16010390

Ejemplares similares

Mechanical property degradation of X80 pipeline steel due to microbiologically influenced corrosion caused by Desulfovibrio vulgaris
por: Li, Zhong, et al.
Publicado: (2022)

Effect of Alternating Current on the Cathodic Protection and Interface Structure of X80 Steel
por: Wang, Huiru, et al.
Publicado: (2017)

Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
por: Li, Zhong, et al.
Publicado: (2017)

Effects of Temperature and Applied Potential on the Stress Corrosion Cracking of X80 Steel in a Xinzhou Simulated Soil Solution
por: Cheng, Yuan, et al.
Publicado: (2022)

Effect of Alternating Current and Sulfate-Reducing Bacteria on Corrosion of X80 Pipeline Steel in Soil-Extract Solution
por: Qing, Yongchang, et al.
Publicado: (2019)

The Corrosion Behavior of AZ91D Magnesium Alloy in Simulated Haze Aqueous Solution
por: Cui, Liying, et al.
Publicado: (2018)

Coupling Effects of pH and Dissolved Oxygen on the Corrosion Behavior and Mechanism of X80 Steel in Acidic Soil Simulated Solution
por: Wang, Shuaixing, et al.
Publicado: (2019)

Effect of Service Environmental Parameters on Electrochemical Corrosion Behavior of L80 Casing Steel
por: Sun, Xiaoguang, et al.
Publicado: (2021)

Effect of SRB and Applied Potential on Stress Corrosion Behavior of X80 Steel in High-pH Soil Simulated Solution
por: Xu, Congmin, et al.
Publicado: (2021)

Corrosion behavior and mechanism of X80 steel in silty soil under the combined effect of salt and temperature
por: Bai, Xiangling, et al.
Publicado: (2021)

Effect of Dissolved Oxygen Concentration on the Microbiologically Influenced Corrosion of Q235 Carbon Steel by Halophilic Archaeon Natronorubrum tibetense
por: Qian, Hongchang, et al.
Publicado: (2019)

Effect of Al–Zn Alloy Coating on Corrosion Fatigue Behavior of X80 Riser Steel
por: Han, Zhongying, et al.
Publicado: (2019)

Study on corrosion behavior of X80 steel under stripping coating by sulfate reducing bacteria
por: Cui, Yan-Yu, et al.
Publicado: (2021)

Effect of H(2)S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint
por: Wang, Xueli, et al.
Publicado: (2022)

Extracellular Electron Transfer Is a Bottleneck in the Microbiologically Influenced Corrosion of C1018 Carbon Steel by the Biofilm of Sulfate-Reducing Bacterium Desulfovibrio vulgaris
por: Li, Huabing, et al.
Publicado: (2015)

pH Effect of Natural Gas Hydrate on X80 Steel Solid—Liquid Phase Scouring Corrosion
por: Deng, Song, et al.
Publicado: (2021)

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film
por: Tan, Zhuowei, et al.
Publicado: (2021)

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions
por: Chen, Jukai, et al.
Publicado: (2022)

Electrochemical and Stress Corrosion Mechanism of Submarine Pipeline in Simulated Seawater in Presence of Different Alternating Current Densities
por: Wu, Wei, et al.
Publicado: (2018)

Silane Coatings for Corrosion and Microbiologically Influenced Corrosion Resistance of Mild Steel: A Review
por: Al-Saadi, Saad, et al.
Publicado: (2022)

Microbiologically Influenced Corrosion of 2707 Hyper-Duplex Stainless Steel by Marine Pseudomonas aeruginosa Biofilm
por: Li, Huabing, et al.
Publicado: (2016)

Effect of Cathodic Protection Potential Fluctuations on the Corrosion of Low-Carbon Steels and Hydrogen Absorption by the Metal in Chloride Solutions with Nearly Neutral pH
por: Marshakov, Andrey I., et al.
Publicado: (2022)

Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment
por: Wang, Liwei, et al.
Publicado: (2018)

Microbiologically Influenced Corrosion of Q235 Carbon Steel by Ectothiorhodospira sp.
por: Qi, Hong, et al.
Publicado: (2022)

Microbiologically influenced corrosion of stainless steel independent of sulfate-reducing bacteria
por: Wakai, Satoshi, et al.
Publicado: (2022)

Effect of Corrosion Temperature on the Corrosion of Q235 Steel and 16Mn Steel in Sodium Aluminate Solutions
por: Quan, Bianli, et al.
Publicado: (2021)

Effect of Nanosized NbC Precipitates on Hydrogen Diffusion in X80 Pipeline Steel
por: Cui, Qiaoqi, et al.
Publicado: (2017)

Imidazoline Gemini Surfactants as Corrosion Inhibitors for Carbon Steel X70 in NaCl Solution
por: Zhuang, Wenchang, et al.
Publicado: (2021)

The Corrosion Inhibition of Montmorillonite Nanoclay for Steel in Acidic Solution
por: AlShamaileh, Ehab, et al.
Publicado: (2023)

Mannich Base as Corrosion Inhibitors for N80 Steel in a CO(2) Saturated Solution Containing 3 wt % NaCl
por: Tang, Mingjin, et al.
Publicado: (2019)

Study on the Corrosion Mechanism of N80 Steel in Simulated Oxygen-Reduced Air Drive Production Wellbores
por: Shi, Baocheng, et al.
Publicado: (2023)

Chitosan/Lignosulfonate Nanospheres as “Green” Biocide for Controlling the Microbiologically Influenced Corrosion of Carbon Steel
por: Rasheed, Pathath Abdul, et al.
Publicado: (2020)

Extracellular Electron Transfer in Microbiologically Influenced Corrosion of 201 Stainless Steel by Shewanella algae
por: Chang, Weiwei, et al.
Publicado: (2023)

The Corrosion Behavior of X100 Pipeline Steel in a Sodium Chloride Solution Containing Magnesium and Calcium
por: Yang, Xiaoning, et al.
Publicado: (2023)

Newly Synthesized Morpholinyl Mannich Bases as Corrosion Inhibitors for N80 Steel in Acid Environment
por: Chen, Yuhao, et al.
Publicado: (2022)

An efficient green ionic liquid for the corrosion inhibition of reinforcement steel in neutral and alkaline highly saline simulated concrete pore solutions
por: Sliem, Mostafa H., et al.
Publicado: (2020)

Electrochemical and thermodynamic study on the corrosion performance of API X120 steel in 3.5% NaCl solution
por: Shahzad, Khuram, et al.
Publicado: (2020)

Porphyrins as Corrosion Inhibitors for N80 Steel in 3.5% NaCl Solution: Electrochemical, Quantum Chemical, QSAR and Monte Carlo Simulations Studies
por: Singh, Ambrish, et al.
Publicado: (2015)

Guar Gum as an Eco-Friendly Corrosion Inhibitor for N80 Carbon Steel under Sweet Environment in Saline Solution: Electrochemical, Surface, and Spectroscopic Studies
por: Palumbo, Gaetano, et al.
Publicado: (2023)

Effect of Pseudomonas aeruginosa on corrosion of X65 pipeline steel
por: Tang, Jianhua, et al.
Publicado: (2022)

Cannot write session to /tmp/vufind_sessions/sess_djc0jeo3eqaqodfoc613eu0v9r