The Effect of Molten Phosphate on Corrosion of 316 Stainless Steel, Alloy 625, and Titanium TA8 in Supercritical Water Oxidation Conditions

The early formation of phosphate oxide formed on 316 stainless steel (316 SS), nickel-based Alloy 625, and titanium alloy TA8 exposed in supercritical water (400 °C, 25 MPa) containing phosphate, chloride, and oxygen was investigated. Phosphate corrosion products of austenitic stainless steel displa...

Descripción completa

Detalles Bibliográficos
Autores principales:	Lin, Zitao, Ren, Pengwei, Zhu, Riguang, Tang, Xingying, Zheng, Youchang, Xu, Tiantian, Wang, Yinghui, Yang, Jianqiao, Cai, Jianjun
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2023
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9822422/ https://www.ncbi.nlm.nih.gov/pubmed/36614734 http://dx.doi.org/10.3390/ma16010395

Ejemplares similares

Effect of Temperature and Impurity Content to Control Corrosion of 316 Stainless Steel in Molten KCl-MgCl(2) Salt
por: Li, Na, et al.
Publicado: (2023)

Corrosion of stainless steels in supercritical water
por: Batelle Memorial Institute. Columbus, OH.
Publicado: (1956)

Radionuclide Tracing Based in situ Corrosion and Mass Transport Monitoring of 316L Stainless Steel in a Molten Salt Closed Loop
por: Wang, Yafei, et al.
Publicado: (2023)

Effect of Grain Refinement on the Corrosion Resistance of 316L Stainless Steel
por: Ura-Bińczyk, Ewa
Publicado: (2021)

Turning Research of Additive Laser Molten Stainless Steel 316L Obtained by 3D Printing
por: Struzikiewicz, Grzegorz, et al.
Publicado: (2019)

Corrosion and microstructural analysis data for AISI 316L and AISI 347H stainless steels after exposure to a supercritical water environment
por: Ruiz, A., et al.
Publicado: (2016)

Datasets on the corrosion behaviour of nanostructured AISI 316 stainless steel treated by SMAT
por: Olugbade, Temitope
Publicado: (2019)

Corrosion Behavior of Incoloy(®)800H, Hastelloy(®)G35(®) and 316L Stainless Steel in the Molten Eutectic Fluoride Mixture FLiNaK and Its Vapors
por: Ramu, Ambati, et al.
Publicado: (2023)

Effects of Titanium-Implanted Dose on the Tribological Properties of 316L Stainless Steel
por: Wang, Wei, et al.
Publicado: (2021)

Corrosion Resistance Measurement of 316L Stainless Steel Manufactured by Selective Laser Melting
por: Guzmán-Nogales, Rigoberto, et al.
Publicado: (2021)

Corrosion Behaviour of 316L Stainless Steel in CNTs–Water Nanofluid: Effect of Temperature
por: Abdeen, Dana H., et al.
Publicado: (2020)

Coupling Effect of Hydrostatic Pressure and Erosion on Corrosion Behavior of X70 Steel in Simulated Seawater
por: Ren, PengWei, et al.
Publicado: (2022)

Corrosion Evaluation of 316L Stainless Steel in CNT-Water Nanofluid: Effect of CNTs Loading
por: Abdeen, Dana H., et al.
Publicado: (2019)

Corrosion and Microstructural Investigation on Additively Manufactured 316L Stainless Steel: Experimental and Statistical Approach
por: Maicas-Esteve, Héctor, et al.
Publicado: (2022)

Revealing the Corrosion Resistance of 316 L Stainless Steel by an In Situ Grown Nano Oxide Film
por: Ren, Ying, et al.
Publicado: (2023)

The effect of duplex Surface mechanical attrition and nitriding treatment on corrosion resistance of stainless steel 316L
por: Li, Nana, et al.
Publicado: (2018)

Stress Corrosion Behaviors of 316LN Stainless Steel in a Simulated PWR Primary Water Environment
por: Huang, Yong, et al.
Publicado: (2018)

The Effect of H(2)S Pressure on the Formation of Multiple Corrosion Products on 316L Stainless Steel Surface
por: Shah, M., et al.
Publicado: (2020)

Stress Corrosion Cracking of 316L Stainless Steel Additively Manufactured with Sinter-Based Material Extrusion
por: Santamaria, Ricardo, et al.
Publicado: (2023)

Susceptibility of 316L Stainless Steel Structures to Corrosion Degradation in Salivary Solutions in the Presence of Lactic Acid
por: Benea, Lidia, et al.
Publicado: (2023)

The corrosion behavior of 304 stainless steel in NaNO(3)–NaCl–NaF molten salt and vapor
por: Lai, Xing, et al.
Publicado: (2022)

Study on cerium-doped nano-TiO(2) coatings for corrosion protection of 316 L stainless steel
por: Li, Suning, et al.
Publicado: (2012)

Corrosion Resistance of AISI 316L Stainless Steel Biomaterial after Plasma Immersion Ion Implantation of Nitrogen
por: Zatkalíková, Viera, et al.
Publicado: (2021)

Influence of Build Angle and Polishing Roughness on Corrosion Resistance of 316L Stainless Steel Fabricated by SLM Method
por: Wang, Hao, et al.
Publicado: (2022)

Corrosion Resistance of Laser Powder Bed Fused AISI 316L Stainless Steel and Effect of Direct Annealing
por: Bae, Kichang, et al.
Publicado: (2022)

Effect of Initial Surface Scratches on the Cavitation Erosion Behavior of 316L Stainless Steel Substrates and 316L Stainless Steel Coatings
por: Lu, Pengfei, et al.
Publicado: (2023)

High temperature corrosion in molten salts
por: Sequeira, César A C
Publicado: (2003)

Corrosion Behavior of AISI 316L Stainless Steel Used as Inner Lining of Bimetallic Pipe in a Seawater Environment
por: Li, Daquan, et al.
Publicado: (2021)

Effect of Laser Speed and Hatch Spacing on the Corrosion Behavior of 316L Stainless Steel Produced by Selective Laser Melting
por: Collazo, Antonio, et al.
Publicado: (2022)

Mechanical, Microstructure, and Corrosion Characterization of Dissimilar Austenitic 316L and Duplex 2205 Stainless-Steel ATIG Welded Joints
por: Touileb, Kamel, et al.
Publicado: (2022)

Corrosion behavior of 316 stainless steel arc parts in liquid lead at 650 °C under high oxygen concentrations
por: Wang, Ruizhong, et al.
Publicado: (2022)

Effect of Thermal Treatment on Corrosion Behavior of AISI 316L Stainless Steel Manufactured by Laser Powder Bed Fusion
por: Andreatta, Francesco, et al.
Publicado: (2022)

Laser Powder Bed Fusion of 316L Stainless Steel: Effect of Laser Polishing on the Surface Morphology and Corrosion Behavior
por: Liu, Jun, et al.
Publicado: (2023)

Influence of Oxygen Content in the Protective Gas on Pitting Corrosion Resistance of a 316L Stainless Steel Weld Joint
por: Maroufkhani, Mohammad, et al.
Publicado: (2023)

Neural network based corrosion modeling of Stainless Steel 316L elbow using electric field mapping data
por: Memon, Azhar M., et al.
Publicado: (2023)

Stress Corrosion Cracking of Additively Manufactured Alloy 625
por: Cabrini, Marina, et al.
Publicado: (2021)

Corrosion Behavior of Niobium-Coated 316L Stainless Steels as Metal Bipolar Plates for Polymer Electrolyte Membrane Fuel Cells
por: Kim, Yu-Sung, et al.
Publicado: (2021)

Assessment of Hot Corrosion in Molten Na(2)SO(4) and V(2)O(5) of Inconel 625 Fabricated by Selective Laser Melting versus Conventional Technology
por: Badea, Teodor Adrian, et al.
Publicado: (2022)

Corrosion of stainless steels /
por: Sedriks, A. John
Publicado: (1996)

Corrosion of stainless steels
por: Sedriks, A John
Publicado: (1996)

Cannot write session to /tmp/vufind_sessions/sess_qsh3ng7u5n9efvdhfqcgtoh6b2