Effect of Pseudomonas aeruginosa on corrosion of X65 pipeline steel

Microbiologically influenced corrosion (MIC) has caused great losses to many industries. This paper aimed to study the corrosion behavior of P. aeruginosa on X65 steel. The corrosion behavior of P. aeruginosa on X65 steel under aerobic and anaerobic conditions was studied by scanning electron micros...

Descripción completa

Detalles Bibliográficos
Autores principales:	Tang, Jianhua, Guo, Ruiqi, Zhang, Xin, Zhao, Xu
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	Elsevier 2022
Materias:	Research Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9834755/ https://www.ncbi.nlm.nih.gov/pubmed/36643323 http://dx.doi.org/10.1016/j.heliyon.2022.e12588

Ejemplares similares

Inhibition Effect of Pseudomonas stutzeri on the Corrosion of X70 Pipeline Steel Caused by Sulfate-Reducing Bacteria
por: Qiu, Lina, et al.
Publicado: (2023)

Anaerobic Corrosion of 304 Stainless Steel Caused by the Pseudomonas aeruginosa Biofilm
por: Jia, Ru, et al.
Publicado: (2017)

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions
por: Yang, Yuanfeng, et al.
Publicado: (2015)

Investigation of erosion-corrosion failure of API X52 carbon steel pipeline
por: Abdu, Mahmoud T., et al.
Publicado: (2023)

Microbiologically Influenced Corrosion of 2707 Hyper-Duplex Stainless Steel by Marine Pseudomonas aeruginosa Biofilm
por: Li, Huabing, et al.
Publicado: (2016)

Effect of H(2)S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint
por: Wang, Xueli, et al.
Publicado: (2022)

Structural Integrity of Steel Pipeline with Clusters of Corrosion Defects
por: Witek, Maciej
Publicado: (2021)

Effect of Alternating Current and Sulfate-Reducing Bacteria on Corrosion of X80 Pipeline Steel in Soil-Extract Solution
por: Qing, Yongchang, et al.
Publicado: (2019)

A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel
por: Yang, Zixuan, et al.
Publicado: (2017)

Effect of Alcaligenes sp. on corrosion behavior of X65 steel in simulated offshore oilfield-produced water
por: Shi, Peiyu, et al.
Publicado: (2023)

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film
por: Tan, Zhuowei, et al.
Publicado: (2021)

The Corrosion Behavior of X100 Pipeline Steel in a Sodium Chloride Solution Containing Magnesium and Calcium
por: Yang, Xiaoning, et al.
Publicado: (2023)

Hydrogen Accumulation and Distribution in Pipeline Steel in Intensified Corrosion Conditions
por: Titov, Anatolii I., et al.
Publicado: (2019)

Correction: Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions. Materials 2015, 8, 2635–2649
por: Yang, Yuanfeng, et al.
Publicado: (2015)

Mechanical property degradation of X80 pipeline steel due to microbiologically influenced corrosion caused by Desulfovibrio vulgaris
por: Li, Zhong, et al.
Publicado: (2022)

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions
por: Chen, Jukai, et al.
Publicado: (2022)

Numerical Simulation of Damage Evolution and Electrode Deformation of X100 Pipeline Steel during Crevice Corrosion
por: Su, Wenxian, et al.
Publicado: (2022)

Prediction of Corrosive Fatigue Life of Submarine Pipelines of API 5L X56 Steel Materials
por: Gao, Xudong, et al.
Publicado: (2019)

Erosion–Corrosion Behavior of Friction Stud Welded Joints of X65 Pipelines in Simulated Seawater under Different Flow Rates
por: Zhao, Jie, et al.
Publicado: (2023)

Research on the Corrosion Behavior of Q235 Pipeline Steel in an Atmospheric Environment through Experiment
por: Cai, Shuo, et al.
Publicado: (2022)

Electrochemical Study on the Macro-Cell Corrosion of Pipeline Steel Partially Covered by Different Kinds of Mineral Deposits
por: He, Limin, et al.
Publicado: (2023)

Corrosion Failure Mechanism of Associated Gas Transmission Pipeline
por: Zhao, Weimin, et al.
Publicado: (2018)

Recent Advances in Nondestructive Method and Assessment of Corrosion Undercoating in Carbon–Steel Pipelines
por: May, Zazilah, et al.
Publicado: (2022)

Anticorrosion Investigation of New Diazene-Based Schiff Base Derivatives as Safe Corrosion Inhibitors for API X65 Steel Pipelines in Acidic Oilfield Formation Water: Synthesis, Experimental, and Computational Studies
por: A Altalhi, Amal
Publicado: (2023)

Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment
por: Wang, Liwei, et al.
Publicado: (2018)

A pipeline to evaluate inhibitors of the Pseudomonas aeruginosa exotoxin U
por: Foulkes, Daniel M., et al.
Publicado: (2021)

Investigation of Hydrogen Embrittlement Susceptibility and Fracture Toughness Drop after in situ Hydrogen Cathodic Charging for an X65 Pipeline Steel
por: Kyriakopoulou, Helen P., et al.
Publicado: (2020)

Effect of Jet Impingement Velocity and Angle on CO(2) Erosion–Corrosion with and without Sand for API 5L-X65 Carbon Steel
por: Toor, Ihsan Ulhaq, et al.
Publicado: (2020)

Underground pipeline corrosion
por: Orazem, Mark
Publicado: (2014)

Analysis of Pipeline Steel Corrosion Data From NBS (NIST) Studies Conducted Between 1922–1940 and Relevance to Pipeline Management
por: Ricker, Richard E.
Publicado: (2010)

On the Corrosion Mechanism of CO(2) Transport Pipeline Steel Caused by Condensate: Synergistic Effects of NO(2) and SO(2)
por: Quynh Hoa, Le, et al.
Publicado: (2019)

Corrosion and hydrogen evolution rate control for X-65 carbon steel based on chitosan polymeric ionic liquids: experimental and quantum chemical studies
por: Elsaeed, S. M., et al.
Publicado: (2018)

Fatigue Life Assessment of API Steel Grade X65 Pipeline Using a Modified Basquin Parameter of the Magnetic Flux Leakage Signal
por: Firdaus, Syed Muhamad, et al.
Publicado: (2023)

Hydrogen Permeation in X65 Steel under Cyclic Loading
por: Cabrini, Marina, et al.
Publicado: (2020)

Coupling Effect of Hydrostatic Pressure and Erosion on Corrosion Behavior of X70 Steel in Simulated Seawater
por: Ren, PengWei, et al.
Publicado: (2022)

Strengthening Effect of Nb on Ferrite Grain Boundary in X70 Pipeline Steel
por: Li, Zhongyi, et al.
Publicado: (2020)

Utilizing birch leaf extract in pickling liquid as a sustainable source of corrosion inhibitor for pipeline steel
por: Mohsen, Q., et al.
Publicado: (2022)

Corrosion of stainless steels /
por: Sedriks, A. John
Publicado: (1996)

Corrosion of stainless steels
por: Sedriks, A John
Publicado: (1996)

Corrosion Behavior on 20# Pipeline Steel by Sulfate-Reducing Bacteria in Simulated NaCl Alkali/Surfactant/Polymer Produced Solution
por: Zhang, Li, et al.
Publicado: (2023)

Cannot write session to /tmp/vufind_sessions/sess_b1ejllradns9vqm00f421q11bs