Evaluation of Biological Pretreatment of Wormwood Rod Reies with White Rot Fungi for Preparation of Porous Carbon

In this work, the wormwood rod residues are pretreated with white rot fungi as the precursor to preparing porous carbon following a simple carbonization and activation process (denoted herein as FWRA sample). The FWRA sample possesses abundant hierarchical pores structure with high specific surface area (1165.7 m(2) g(−1)) and large pore volume (1.02 cm(3) g(−1)). As an electrode for supercapacitors, the FWRA sample offers a high specific capacitance of 443.2 F g(−1) at 0.5 A g(−1) and superb rate ability holding a specific capacitance of 270 F g(−1) at 100 A g(−1) in 6 M KOH electrolyte. The corresponding symmetrical capacitor has a superb cyclic stability with a low specific capacitance decay rate of 0.4% after 20,000 cycles at 5 A g(−1) in 1 M Na(2)SO(4) electrolyte. Moreover, measurements revealed that when used as adsorbent, the FWRA sample is ideal for removing methyl orange (MO) from water, exhibiting a superior adsorption ability of 260.8 mg g(−1). Therefore, this study is expected to provide a simple and environmentally friendly technique for the generation of value-added and functional porous carbon materials from Chinese medicinal herbal residues, thus offering promising candidates for broad application areas.