Investigating Different Local Polyurethane Coatings Degradation Effects and Corrosion Behaivors by Talaromyces funiculosus via Wire Beam Electrodes
The degradation effect of mold on the coating in a hot and humid environment is one of the important factors that cause layer failure. Combined with the wire beam electrode (WBE) and the traditional surface analysis technique, the local biodegradation of the coatings and the corrosion behaviors of m...
Autores principales: | Hao, Xiangping, Yang, Kexin, Yuan, Yiding, Zhang, Dawei, Lu, Lin |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2023
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC9964212/ https://www.ncbi.nlm.nih.gov/pubmed/36837032 http://dx.doi.org/10.3390/ma16041402 |
Ejemplares similares
-
Insight into Degrading Effects of Two Fungi on Polyurethane Coating Failure in a Simulated Atmospheric Environment
por: Hao, Xiangping, et al.
Publicado: (2023) -
Aniline-induced production of aniline-containing polyketides and related bicyclic polyketides by the Yellow River wetland-derived fungus Talaromyces funiculosus
por: Wang, Zhenhui, et al.
Publicado: (2023) -
Polyurethane spray coating of aluminum wire bonds to prevent corrosion and suppress resonant oscillations
por: Izen, Joseph, et al.
Publicado: (2015) -
Polyurethane spray coating of aluminum wire bonds to prevent corrosion and suppress resonant oscillations
por: Izen, Joseph M., et al.
Publicado: (2015) -
A study on the local corrosion behavior and mechanism of electroless Ni–P coatings under flow by using a wire beam electrode
por: Tang, Yi-Rong, et al.
Publicado: (2019)