Development and Application of Poly (Lactic Acid)/Poly (Butylene Adipate-Co-Terephthalate)/Thermoplastic Starch Film Containing Salicylic Acid for Banana Preservation

Bananas are susceptible to the effects of endogenous enzymatic, leading to their rapid decay and deterioration. In order to mitigate economic losses and prolong the shelf life of bananas, the objective of this study was to develop a new and green gas-regulating packaging film. In this study, an active gas-regulating packaging film was prepared by extrusion, with mobil composition of matter (MCM)-41 loaded with salicylic acid (SA) as the active agent and poly (lactic acid) (PLA), poly (butylene adipate-co-terephthalate) (PBAT), and thermoplastic starch (TPS) as the base materials. The obtained films included PLA/PBAT/TPS, PLA/PBAT/TPS-SA, and PLA/PBAT/TPS-MCSA. These films were subsequently applied to banana preservation. The study focused on the variations in soluble solid content (SSC), rate of weight loss (RWL), malondialdehyde (MDA) content, and polyphenol oxidase (PPO) activity of bananas during the preservation process. The results showed that, compared with the PLA/PBAT/TPS film, the oxygen transmission rate of the PLA/PBAT/TPS-MCSA film increased from 384.36 ± 22.06 cm(3)·m(−2)·24 h(−1)·0.1 MPa(−1) to 543.10 ± 3.47 cm(3)·m(−2)·24 h(−1)·0.1 MPa(−1). Throughout the preservation period, the PLA/PBAT/TPS-MCSA film exhibited superior performance, effectively retarding the increase in banana SSC, RWL, and MDA while inhibiting the elevation of PPO activity and prolonging the shelf life of bananas by 4–5 days. However, this study needs to further investigate the mechanism of function of MCM-41 loaded with SA in banana preservation.