'Wagon-wheel' mask as a tool to study anisotropy of porous silicon formation rate

Relationship between the rate of electrochemical formation of mesoporous Si and the crystallographic directions has been studied by local anodization of wafers through a mask having the form of narrow long wedges radiating from the center in all directions (‘wagon-wheel’ mask). The etching rates were found from the side etching under the thin transparent n-Si mask. On p(+)-substrates of various orientation diagrams characterizing the distribution of pore formation rates over different directions in the wafer plane were constructed for the first time. The wagon-wheel method was applied to study the current dependence of the anisotropy. It was found that the orientation-related difference between the pore formation rates is 5% to 25%, depending on the crystallographic direction and the etching current density. At a current density of approximately 9 mA/cm(2), the etching rates are related as V100:V113:V110:V112:V111 = 1.000:0.900:0.836:0.824:0.750. A general tendency is observed toward weakening of the anisotropy with increasing current. The highest rate always corresponds to the <100 > direction, and the rate ratio between the other directions varies with increasing current, which leads to a change of their sequence.