Statistical study of ductility-dip cracking induced plastic deformation in polycrystalline laser 3D printed Ni-based superalloy

Ductility-dip cracking in Ni-based superalloy, resulting from heat treatment, is known to cause disastrous failure, but its mechanism is still not completely clear. A statistical study of the cracking behavior as a function of crystal orientation in a laser 3D-printed DL125L Ni-based superalloy poly...

Descripción completa

Detalles Bibliográficos
Autores principales: Qian, Dan, Xue, Jiawei, Zhang, Anfeng, Li, Yao, Tamura, Nobumichi, Song, Zhongxiao, Chen, Kai
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Nature Publishing Group UK 2017
Materias:
Article
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5460225/
https://www.ncbi.nlm.nih.gov/pubmed/28588298
http://dx.doi.org/10.1038/s41598-017-03051-x

Internet

https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5460225/
https://www.ncbi.nlm.nih.gov/pubmed/28588298
http://dx.doi.org/10.1038/s41598-017-03051-x

Ejemplares similares