Remaining Life Assessment for Steel After Low-Cycle Fatigue by Surface Crack Image
After pre-fatigue cycles at different strain amplitudes with different N/N(f) values (33.3%, 50%, and 75%), specimens of HRB335 steel were subjected to uniaxial tension until failure. By this method the mechanical properties of the specimens after pre-fatigue testing were measured, and the fracture...
Autores principales: | Shi, Che-Si, Zeng, Bin, Liu, Gui-Long, Zhang, Ke-Shi |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2019
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6427471/ https://www.ncbi.nlm.nih.gov/pubmed/30862079 http://dx.doi.org/10.3390/ma12050823 |
Ejemplares similares
-
Acoustic Emission Monitoring of Fatigue Crack Growth in Hadfield Steel
por: Shi, Shengrun, et al.
Publicado: (2023) -
Influence of Strain Gradient on Fatigue Life of Carbon Steel for Pressure Vessels in Low-Cycle and High-Cycle Fatigue Regimes
por: Fujii, Tomoyuki, et al.
Publicado: (2022) -
Prediction of Crack Initiation Based on Energy Storage Rate during Low-Cycle Fatigue of Austenitic Stainless Steel
por: Grodzki, Wojciech, et al.
Publicado: (2021) -
Healing of Fatigue Crack in 1045 Steel by Using Eddy Current Treatment
por: Yang, Chuan, et al.
Publicado: (2016) -
Evaluation of Thermal Fatigue Life and Crack Morphology in Brake Discs of Low-Alloy Steel for High-Speed Trains
por: Wang, Jinnan, et al.
Publicado: (2022)