The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile

In the present work, the localized corrosion and stress corrosion cracking (SCC) behaviors of a commercial 6005A-T6 aluminum extrusion profile was studied comprehensively. The velocity of crack growth in self-stressed double-cantilever beam (DCB) specimens under constant displacement was estimated,...

Descripción completa

Detalles Bibliográficos
Autores principales: Ma, Jijun, Sun, Jing, Guan, Quanmei, Yang, Qingwei, Tang, Jian, Zou, Chengxiong, Wang, Jun, Tang, Bin, Kou, Hongchao, Wang, Haisheng, Gao, Jun, Li, Jinshan, Wang, William Yi
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2021
Materias:
Article
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8434543/
https://www.ncbi.nlm.nih.gov/pubmed/34501014
http://dx.doi.org/10.3390/ma14174924

Internet

https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8434543/
https://www.ncbi.nlm.nih.gov/pubmed/34501014
http://dx.doi.org/10.3390/ma14174924

Ejemplares similares