The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile

In the present work, the localized corrosion and stress corrosion cracking (SCC) behaviors of a commercial 6005A-T6 aluminum extrusion profile was studied comprehensively. The velocity of crack growth in self-stressed double-cantilever beam (DCB) specimens under constant displacement was estimated,...

Descripción completa

Detalles Bibliográficos
Autores principales:	Ma, Jijun, Sun, Jing, Guan, Quanmei, Yang, Qingwei, Tang, Jian, Zou, Chengxiong, Wang, Jun, Tang, Bin, Kou, Hongchao, Wang, Haisheng, Gao, Jun, Li, Jinshan, Wang, William Yi
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2021
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8434543/ https://www.ncbi.nlm.nih.gov/pubmed/34501014 http://dx.doi.org/10.3390/ma14174924

Ejemplares similares

Pitting Corrosion of Natural Aged Al–Mg–Si Extrusion Profile
por: Guan, Quanmei, et al.
Publicado: (2019)

Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking
por: Wang, Wenwen, et al.
Publicado: (2015)

Stress Corrosion Cracking of 316L Stainless Steel Additively Manufactured with Sinter-Based Material Extrusion
por: Santamaria, Ricardo, et al.
Publicado: (2023)

Corrosion Crack Morphology and Creep Analysis of Members Based on Meso-Scale Corrosion Penetration
por: Zeng, Bin, et al.
Publicado: (2022)

A Crack Propagation Method for Pipelines with Interacting Corrosion and Crack Defects
por: Xie, Mingjiang, et al.
Publicado: (2022)

Fatigue Property and Small Crack Propagation Mechanism of MIG Welding Joint of 6005A-T6 Aluminum Alloy
por: Peng, Zeng, et al.
Publicado: (2022)

Prediction of Crack Width in RC Piles Exposed to Local Corrosion in Chloride Environment
por: Shao, Wei, et al.
Publicado: (2023)

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete
por: Ji, Haodong, et al.
Publicado: (2020)

Stress Corrosion Cracking of Additively Manufactured Alloy 625
por: Cabrini, Marina, et al.
Publicado: (2021)

Influence of Chloride Concentration on Stress Corrosion Cracking and Crevice Corrosion of Austenitic Stainless Steel in Saline Environments
por: Yeh, Chun-Ping, et al.
Publicado: (2020)

Corrosion Behavior and Susceptibility to Stress Corrosion Cracking of Leaded and Lead-Free Brasses in Simulated Drinking Water
por: Choucri, Jamal, et al.
Publicado: (2021)

Concrete Cover Cracking and Reinforcement Corrosion Behavior in Concrete with New-to-Old Concrete Interfaces
por: Zhang, Juhui, et al.
Publicado: (2023)

Microstructure and Pitting Corrosion of Austenite Stainless Steel after Crack Arrest
por: Zhang, Zhuwu, et al.
Publicado: (2019)

Concrete Cracking Prediction Including the Filling Proportion of Strand Corrosion Products
por: Wang, Lei, et al.
Publicado: (2016)

A Monitoring Method Based on FBG for Concrete Corrosion Cracking
por: Mao, Jianghong, et al.
Publicado: (2016)

Laboratory-Based Investigation into Stress Corrosion Cracking of Cable Bolts
por: Wu, Saisai, et al.
Publicado: (2019)

Effect of Zn/Mg Ratios on Microstructure and Stress Corrosion Cracking of 7005 Alloy
por: Wang, Shuai, et al.
Publicado: (2019)

A Comparative Study of Localized Corrosion and Stress Corrosion Cracking of 13Cr Martensitic Stainless Steel Using Acoustic Emission and X-ray Computed Tomography
por: Wu, Kaige, et al.
Publicado: (2019)

Corrosion and corrosion control : an introduction to corrosion science and engineering /
por: Revie, R. Winston (Robert Winston), 1944-
Publicado: (2008)

Corrosion and corrosion control: An introduction to corrosion science and engineering
por: Uhlig, Herbert Henry, 1907-
Publicado: (1985)

A Study on the Influential Factors of Stress Corrosion Cracking in C110 Casing Pipe
por: Wang, Zhe, et al.
Publicado: (2022)

Concrete Protective Layer Cracking Caused by Non-Uniform Corrosion of Reinforcements
por: Zhang, Lu, et al.
Publicado: (2019)

Modelling of Corrosion-Induced Concrete Cover Cracking Due to Chloride Attacking
por: Lun, Pei-Yuan, et al.
Publicado: (2021)

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines
por: Zhang, Ci, et al.
Publicado: (2022)

Effect of Aging Treatment on the Corrosion Resistance Properties of 7N01 Extrusion Aluminum Alloy
por: Li, Yitai, et al.
Publicado: (2021)

Influence of Rare Earth Element (Y) on Microstructure and Corrosion Behavior of Hot Extrusion AZ91 Magnesium Alloy
por: Cui, Yanan, et al.
Publicado: (2020)

Effect of Air Storage on Stress Corrosion Cracking of ZK60 Alloy Induced by Preliminary Immersion in NaCl-Based Corrosion Solution
por: Merson, Evgeniy, et al.
Publicado: (2022)

Effect of Ion Corrosion on 517 Phase Stability
por: Wang, Guijia, et al.
Publicado: (2020)

Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions
por: Singh Raman, R. K., et al.
Publicado: (2014)

Corrosion-Fatigue Crack Growth in Plates: A Model Based on the Paris Law
por: Toribio, Jesús, et al.
Publicado: (2017)

Stress Corrosion Cracking of Friction Stir-Welded AA-2024 T3 Alloy
por: Cabrini, Marina, et al.
Publicado: (2020)

Numerical Investigation on Lateral Confinement Effects on Concrete Cracking Induced by Rebar Corrosion
por: Choe, Gyeongcheol, et al.
Publicado: (2020)

A probabilistic computational framework for the prediction of corrosion-induced cracking in large structures
por: Qian, Guofeng, et al.
Publicado: (2022)

Cracking in Reinforced Concrete Cross-Sections Due to Non-Uniformly Distributed Corrosion
por: German, Magdalena, et al.
Publicado: (2023)

Corrosión y control de corrosión
por: Uhlig, Herbert Henry, 1907-
Publicado: (1979)

Age Hardening of Extruded AA 6005A Aluminium Alloy Powders
por: Feijoo, Iria, et al.
Publicado: (2019)

Corrosion Inhibition Coating Based on the Self-Assembled Polydopamine Films and Its Anti-Corrosion Properties
por: Li, Shanjian, et al.
Publicado: (2022)

Effects of Multi-Pass Turning on Stress Corrosion Cracking of AISI 304 Austenitic Stainless Steel
por: Zhang, Yansong, et al.
Publicado: (2022)

Welding Defect and Mechanical Properties of Nanosecond Laser Cleaning 6005A Aluminum Alloy
por: Zhang, Yuelai, et al.
Publicado: (2022)

Corrosión
por: Galvele, José R.
Publicado: (1979)

Cannot write session to /tmp/vufind_sessions/sess_l3clpa6sjooq7u11iamqt439jg