Hydrogen-Induced Cracking Caused by Galvanic Corrosion of Steel Weld in a Sour Environment

This study examined the hydrogen-induced cracking (HIC) caused by galvanic corrosion of an ASTM A516-65 steel weld in a wet sour environment using a combination of standard immersion corrosion test, electrochemical analyses, and morphological observation of corrosion damage. This study showed that t...