Engineering the Crack Structure and Fracture Behavior in Monolayer MoS(2) By Selective Creation of Point Defects

Monolayer transition‐metal dichalcogenides, e.g., MoS(2), typically have high intrinsic strength and Young's modulus, but low fracture toughness. Under high stress, brittle fracture occurs followed by cleavage along a preferential lattice direction, leading to catastrophic failure. Defects have...